Table 1 The values of various parameters (sample diameter D, coating time, coating thickness, yield strength σY, plastic strain before fracture εp, average shear slip size 
and maximum shear slip size 
) for different MG samples.
and maximum shear slip size 
) for different MG samples.From: Origin of Shear Stability and Compressive Ductility Enhancement of Metallic Glasses by Metal Coating
MGs | D (mm) | Coating time (min) | Coating Thickness (μm) | σY(MPa) | εp(%) |
|
|
|---|---|---|---|---|---|---|---|
Vit105 | 2 | 0 | 0 | 1736 | 3.95 | 2.39 | 5.32 |
Vit105 | 2 | 45 | 21.68 | 1708 | 14.77 | 1.36 | 5.40 |
Vit105 | 3 | 0 | 0 | 1755 | 0.34 | – | – |
Vit105 | 3 | 15 | 9.27 | 1726 | 4.21 | 2.08 | 5.73 |
Vit105 | 3 | 90 | 40.19 | 1697 | 3.58 | 1.64 | 5.81 |
Zr65Cu15Ni10Al10 | 2 | 0 | 0 | 1724 | 2.67 | 2.23 | 5.28 |
Zr65Cu15Ni10Al10 | 2 | 45 | 24.26 | 1701 | 4.07 | 2.01 | 5.39 |
Zr65Cu15Ni10Al10 | 3 | 0 | 0 | 1746 | 0.40 | – | – |
Zr65Cu15Ni10Al10 | 3 | 45 | 24.08 | 1706 | 6.22 | 2.07 | 5.84 |