Figure 5 | Scientific Reports

Figure 5

From: Growth of Co2FeAl Heusler alloy thin films on Si(100) having very small Gilbert damping by Ion beam sputtering

Figure 5

(a) MOKE hysteresis loops recorded at room temperature along the easy axis of magnetization for the CFA films deposited at different Ts. (b) Angle dependent MOKE hysteresis curves recorded at different azimuthal angles on the Si/CFA (53 nm)/Ta (2 nm) thin film deposited at Ts ~ 573 K. (c) Dependence of Hc and Mson Ts (lines serve as guide to the eye).