Figure 2
From: A new (Ba, Ca) (Ti, Zr)O3 based multiferroic composite with large magnetoelectric effect
(a) Temperature dependence of the real part of the electric permittivity of the BCZT85-CFO15 composite measured at different frequencies (see Supplementary Information Fig. S1 for ε′′(T) measured in the frequency range from 10 Hz to 1 MHz). (b) Temperature dependence of real part of the electric permittivity for pure CFO measured at different frequencies from 10 Hz to 1 MHz range. (c) Temperature dependence of the electric permittivity for single phase BCZT ceramics. (d) Frequency dependence of the real part of electric permittivity for CFO, single phase BCZT and the BCZT85-CFO15 composite measured at 300 K. Arrows point in the direction of increasing frequency.