Figure 5
From: Plasticity mechanisms in HfN at elevated and room temperature
TEM images of HfN deformed at 2300 °C (a) Compiled TEM images of dislocations under various two-beam conditions. (b,c) Two-beam images of networking dislocations (d,e) Two-beam visible conditions, where the dislocations of interest are indicated by white arrows of dislocations, with b = a/2 [101] on the 
slip plane piling up at a grain boundary under the two-beam condition g = 
. The corresponding invisible two-beam conditions, (f) g = 020 (g) g = 
. A second set of HT dislocation with b = a/2 
on the (011) slip plane with corresponding two-beam conditions in the inset. The dislocation of interest is indicated again with white arrows in the two visible conditions (h) with g = 020 and (i) g = 
and the corresponding invisible conditions (j) g = 
and (k) g = 
.