Table 1 Chemical compositions of the CoCrFeNiTi0.4 HEA at different states (at. %), as-cast (AC), heat affected zone (HAZ), laser remelted zone (LR), furnace cooling after annealed at 900 °C (FC2).
From: Kinetic ways of tailoring phases in high entropy alloys
States | Phases | Co | Cr | Fe | Ni | Ti |
|---|---|---|---|---|---|---|
AC | FCC | 22.52 | 26.08 | 26.08 | 20.72 | 4.61 |
Laves | 21.99 | 22.29 | 22.19 | 22.77 | 10.76 | |
R | 20.17 | 13.28 | 14.29 | 35.87 | 16.40 | |
HAZ | FCC | 20.51 | 26.21 | 25.93 | 22.62 | 4.73 |
Laves | 21.99 | 23.29 | 22.49 | 22.52 | 9.71 | |
LR | FCC | 22.48 | 23.69 | 23.79 | 22.13 | 7.92 |
Laves | 22.43 | 24.47 | 23.67 | 21.23 | 8.19 | |
FC2 | FCC | 25.10 | 22.70 | 26.27 | 19.02 | 6.91 |
Laves | 20.00 | 42.15 | 25.23 | 7.65 | 4.97 | |
R | 22.54 | 5.29 | 8.11 | 43.79 | 20.27 | |
σ | 24.00 | 22.16 | 21.31 | 22.26 | 10.28 |