Figure 1 | Scientific Reports

Figure 1

From: Dislocation Strengthening without Ductility Trade-off in Metastable Austenitic Steels

Figure 1

Microstructural characterization of warm-rolled metastable austenitic steels.

Two-beam bright field TEM images of TMT samples with (a) 10% and (b) 20% thickness reduction. Zone axis is (110) andg = (111). Scale bar: 100 nm. (c) (EBSD) image of the TMT sample with 20% thickness reduction. Scale bar: 100 um. (d) The responding pole figure of (c) showing weak texture characteristics.

Back to article page