Figure 5: Temperature vs. time plots of the CMC60MTM40-coated fabrics and the control at different sample height during bench-scale VFT. | Scientific Reports

Figure 5: Temperature vs. time plots of the CMC60MTM40-coated fabrics and the control at different sample height during bench-scale VFT.

From: Large-scale, thick, self-assembled, nacre-mimetic brick-walls as fire barrier coatings on textiles

Figure 5

(a–c) Temperature profiles of the control, CMC60MTM40-1.75%, and CMC60MTM40-2.5% at 10, 50, 100, 120 and 150 mm sample height. (d,f) Comparative study of the temperature profiles of all CMC60MTM40-coated fabrics at (d) 50 and (f) 100 mm. (e) FLIR images of CMC60MTM40-1.75% and CMC60MTM40-2.5% corresponding to the first temperature peak at ca. 5 s (hot gas) and second temperature peak at 50 s and 65 s, respectively, (glowing frontier), (temperature scale bar same as in Fig. 4b).