Figure 5: Deformation evolution of Cu(1 1 19) deformed in tension.

(a) Stacking faults nucleate at the surface, (b) growing to the bottom of the sample. (c) The perpendicular slip system is not activated, instead deformation mechanism switches to twinning. Atoms comprising surfaces and stacking faults are shown, others (CS < 2) are removed for clarity.