Figure 5
From: Novel Heating-Induced Reversion during Crystallization of Al-based Glassy Alloys
Bright-field TEM image (a), selected-area electron diffraction pattern (b) and HREM image (c) of the initially fully glassy alloy Al84Y9Ni4Co1.5Fe0.5Pd1 annealed for 300 s at 620 K corresponding to the second exothermic peak (Fig. 1).