Photooxidation and fragmentation behaviors of itPP were studied. Photooxidation likely occurred in the amorphous regions of itPP due to the higher oxygen diffusion. Surface deterioration was observed on the UV-exposed itPP films. Pressed films exhibited much denser cracks compared to uniaxially oriented itPP films. Notably, cracks in the uniaxially oriented itPP films were formed along the direction of orientation and decreased with increasing draw ratio. The crystalline structure and oriented molecular chains notably inhibited the photooxidative degradation and fragmentation of the itPP films.