Abstract
Poly(vinylidene fluoride) (PVdF) and polyaniline (PAni) were partially sulfonated using chlorosulfonic acid (CSA) as the sulfonating agent. Partially sulfonated PVdF (SPVdF) having a degree of sulfonation (DS) of ~22% and partially sulfonated PAni (SPAni) having a DS of ~29% were blended at constituent wt% ratios of SPVdF:SPAni=95:5, 90:10, 85:15 and 80:20 to fabricate different blend membranes. These blend membranes exhibited extremely low methanol uptake and methanol permeability, as well as high membrane selectivity ratios (especially at high methanol concentrations). The blend membranes also exhibited superior water uptake capacity, water swellability, ion-exchange capacity (IEC) and proton conductivity compared with pristine PVdF and SPVdF membranes. The SPVdF:SPAni (80:20) blend membrane was found to produce the lowest methanol permeability values of 1.50 × 10−9 cm2 s−1 (at 2 m methanol) and 6.30 × 10−9 cm2 s−1 (at 8 m methanol) and the highest membrane selectivity values of 3.27 × 106 Ss cm−3 (at 2 m methanol) and 7.78 × 105 Ss cm−3 (at 8 m methanol). However, the introduction of Nafion to the SPVdF/SPAni blend membrane to form a ternary blend membrane (that is, SPVdF:Nafion:SPAni=50:30:20) resulted in much improved IEC and proton conductivity.
Similar content being viewed by others
Log in or create a free account to read this content
Gain free access to this article, as well as selected content from this journal and more on nature.com
or
References
Dutta, K., Kumar, P., Das, S. & Kundu, P. P. Utilization of conducting polymers in fabricating polymer electrolyte membranes for application in direct methanol fuel cells. Polym. Rev. 54, 1–32 (2014).
Zhang, H. & Shen, P. K. Recent development of polymer electrolyte membranes for fuel cells. Chem. Rev. 112, 2780–2832 (2012).
Zhang, H., Huang, H. & Shen, P. K. Methanol-blocking Nafion composite membranes fabricated by layer-by-layer self-assembly for direct methanol fuel cells. Int. J. Hydrogen Energy 37, 6875–6879 (2012).
Zhao, C., Lin, H., Zhang, Q. & Na, H. Layer-by-layer self-assembly of polyaniline on sulfonated poly(arylene ether ketone) membrane with high proton conductivity and low methanol crossover. Int. J. Hydrogen Energy 35, 10482–10488 (2010).
Ahn, K., Kim, M., Kim, K., Oh, I., Ju, H. & Kim, J. Low methanol permeable crosslinked sulfonated poly(phenylene oxide) membranes with hollow glass microspheres for direct methanol fuel cells. Polymer 56, 178–188 (2015).
Ahn, K., Kim, M., Kim, K., Ju, H., Oh, I. & Kim, J. Fabrication of low-methanol-permeability sulfonated poly(phenylene oxide) membranes with hollow glass microspheres for direct methanol fuel cells. J. Power Sources 276, 309–319 (2015).
Wang, C.-H., Chen, C.-C., Hsu, H.-C., Du, H.-Y., Chen, C.-P., Hwang, J.-Y., Chen, L. C., Shih, H.-C., Stejskal, J. & Chen, K. H. Low methanol-permeable polyaniline/Nafion composite membrane for direct methanol fuel cells. J. Power Sources 190, 279–284 (2009).
Kumar, P., Dutta, K., Das, S. & Kundu, P. P. An overview of unsolved deficiencies of direct methanol fuel cell technology: factors and parameters affecting its widespread use. Int. J. Energy Res. 38, 1367–1390 (2014).
Dutta, K., Das, S. & Kundu, P. P. Synthesis, preparation and performance of blends and composites of π-conjugated polymers and their copolymers in DMFCs. Polym. Rev. 55, 630–677 (2015).
Cho, K.-Y., Jung, H.-Y., Sung, K. A., Kim, W.-K., Sung, S.-J., Park, J.-K., Choi, J.-H. & Sung, Y.-E. Preparation and characteristics of Nafion membrane coated with a PVdF copolymer/recast Nafion blend for direct methanol fuel cell. J. Power Sources 159, 524–528 (2006).
Cho, K.-Y., Eom, J.-Y., Jung, H.-Y., Choi, N.-S., Lee, Y. M., Park, J.-K., Choi, J.-H., Park, K.-W. & Sung, Y.-E. Characteristics of PVdF copolymer/Nafion blend membrane for direct methanol fuel cell (DMFC). Electrochim. Acta 50, 583–588 (2004).
Kumar, G. G., Lee, D. N., Kim, P., Nahm, K. S. & Elizabeth, R. N. Characterization of PVdF-HFP/Nafion/AlO[OH]n composite membranes for direct methanol fuel cell (DMFC). Eur. Polym. J. 44, 2225–2230 (2008).
Pereira, F., Chan, A., Vallé, K., Palmas, P., Bigarré, J., Belleville, P. & Sanchez, C Design of interpenetrated networks of mesostructured hybrid silica and nonconductive poly(vinylidene fluoride)-cohexafluoropropylene (PVdF-HFP) polymer for proton exchange membrane fuel cell applications. Chem. Asian J. 6, 1217–1224 (2011).
Kumar, G. G., Shin, J., Nho, Y.-C., seon Hwang, I., Fei, G., Kim, A. R. & Nahm, K. S. Irradiated PVdF-HFP-tin oxide composite membranes for the applications of direct methanol fuel cells. J. Membr. Sci. 350, 92–100 (2010).
Corti, H. R. & Gonzalez, E. R. (eds). Direct Alcohol Fuel Cells: Materials, Performance, Durability and Applications IX, 370 (Springer, Netherlands, 2014)
Li, M., Zhang, G., Xu, S., Zhao, C., Han, M., Zhang, L., Jiang, H., Liu, Z. & Na, H. Cross-linked polyelectrolyte for direct methanol fuel cells applications based on a novel sulfonated cross-linker. J. Power Sources 255, 101–107 (2014).
Xu, D., Zhang, G., Zhang, N., Li, H., Zhang, Y., Shao, K., Han, M., Lew, C. M. & Na, H. Surface modification of heteropoly acid/SPEEK membranes by polypyrrole with a sandwich structure for direct methanol fuel cells. J. Mater. Chem. 20, 9239–9245 (2010).
Neelakandan, S., Rana, D., Matsuura, T., Muthumeenal, A., Kanagaraj, P. & Nagendran, A. Fabrication and electrochemical properties of surface modified sulfonated poly(vinylidenefluoride-co-hexafluoropropylene) membranes for DMFC application. Solid State Ionics 268, 35–41 (2014).
Mokrini, A. & Huneault, M. A. Proton exchange membranes based on PVDF/SEBS blends. J. Power Sources 154, 51–58 (2006).
Zhang, Y., Cai, W., Si, F., Ge, J., Liang, L., Liu, C. & Xing, W. A modified Nafion membrane with extremely low methanol permeability via surface coating of sulfonated organic silica. Chem. Commun. 48, 2870–2872 (2012).
Diaz, L. A., Abuin, G. C. & Corti, H. R. Methanol sorption and permeability in Nafion and acid-doped PBI and ABPBI membranes. J. Membr. Sci. 411-412, 35–44 (2012).
Peighambardoust, S. J., Rowshanzamir, S. & Amjadi, M. Review of the proton exchange membranes for fuel cell applications. Int. J. Hydrogen Energy 35, 9349–9384 (2010).
Sahu, A. K., Bhat, S. D., Pitchumani, S., Sridhar, P., Vimalan, V., George, C., Chandrakumar, N. & Shukla, A. K. Novel organic-inorganic composite polymer-electrolyte membranes for DMFCs. J. Membr. Sci. 345, 305–314 (2009).
Ahmed, M. & Dincer, I. A review on methanol crossover in direct methanol fuel cells: challenges and achievements. Int. J. Energy Res. 35, 1213–1228 (2011).
Liu, F., Hashim, N. A., Liu, Y., Abed, M. R. M. & Li, K. Progress in the production and modification of PVDF membranes. J. Membr. Sci. 375, 1–27 (2011).
Kumar, P., Dutta, K., Das, S. & Kundu, P. P. Membrane prepared by incorporation of crosslinked sulfonated polystyrene in the blend of PVdF-co-HFP/Nafion: a preliminary evaluation for application in DMFC. Appl. Energy 123, 66–74 (2014).
Das, S., Kumar, P., Dutta, K. & Kundu, P. P. Partial sulfonation of PVdF-co-HFP: a preliminary study and characterization for application in direct methanol fuel cell. Appl. Energy 113, 169–177 (2014).
Dutta, K., Das, S., Kumar, P. & Kundu, P. P. Polymer electrolyte membrane with high selectivity ratio for direct methanol fuel cells: a preliminary study based on blends of partially sulfonated polymers polyaniline and PVdF-co-HFP. Appl. Energy 118, 183–191 (2014).
Dutta, K., Das, S. & Kundu, P. P. Low methanol permeable and highly selective membranes composed of pure and/or partially sulfonated PVdF-co-HFP and polyaniline. J. Membr. Sci. 468, 42–51 (2014).
Dutta, K., Das, S. & Kundu, P. P. Partially sulfonated polyaniline induced high ion-exchange capacity and selectivity of Nafion membrane for application in direct methanol fuel cells. J. Membr. Sci. 473, 94–101 (2015).
Mondal, S., Soam, S. & Kundu, P. P. Reduction of methanol crossover and improved electrical efficiency in direct methanol fuel cell by the formation of a thin layer on Nafion 117 membrane: effect of dip-coating of a blend of sulphonated PVdF-co-HFP and PBI. J. Membr. Sci. 474, 140–147 (2015).
Das, S., Dutta, K. & Kundu, P. P. Partially sulfonated poly(vinylidene fluoride) induced enhancements of properties and DMFC performance of Nafion electrolyte membrane. Fuel Cells 15, 505–515 (2015).
Dutta, K., Mahale, R. Y., Arulkashmir, A. & Krishnamoorthy, K. Reversible assembly and disassembly of micelles by a polymer that switches between hydrophilic and hydrophobic wettings. Langmuir 28, 10097–10104 (2012).
Das, S., Dutta, K. & Kundu, P. P. Nickel nanocatalysts supported on sulfonated polyaniline: potential toward methanol oxidation and as anode materials for DMFCs. J. Mater. Chem. A 3, 11349–11357 (2015).
Kumar, P., Dutta, K. & Kundu, P. P. Enhanced performance of direct methanol fuel cells: a study on the combined effect of various supporting electrolytes, flow channel designs and operating temperatures. Int. J. Energy Res. 38, 41–50 (2014).
Becker, C. M., Biagini, A. B., Forte, M. M. C., Amico, S. C., Vargas, J. V. C. & Azambuja, D. S. Sulfonation and characterization of styrene-indene copolymers for the development of proton conducting polymer membranes. Polímeros 22, 395–400 (2012).
Li, X., Liu, C., Lu, H., Zhao, C., Wang, Z., Xing, W. & Na, H. Preparation and characterization of sulfonated poly(ether ether ketone ketone) proton exchange membranes for fuel cell application. J. Membr. Sci. 255, 149–155 (2005).
Nasef, M. M. & Aly, A. A. Water and charge transport models in proton exchange membranes: an overview. Desalination 287, 238–246 (2012).
Kreuer, K.-D. Proton conductivity: materials and applications. Chem. Mater. 8, 610–641 (1996).
Song, M.-K., Kim, Y.-T., Fenton, J. M., Kunz, H. R. & Rhee, H.-W. Chemically-modified Nafion®/poly(vinylidene fluoride) blend ionomers for proton exchange membrane fuel cells. J. Power Sources 117, 14–21 (2003).
Zhou, H., Wang, H., Niu, H., Gestos, A. & Lin, T. Robust, self-healing superamphiphobic fabrics prepared by two-step coating of fluoro-containing polymer, fluoroalkyl silane, and modified silica nanoparticles. Adv. Funct. Mater. 23, 1664–1670 (2013).
Kim, H. J., Kim, H. J., Shul, Y. G. & Han, H. S. Nafion-Nafion/polyvinylidene fluoride-Nafion laminated polymer membrane for direct methanol fuel cells. J. Power Sources 135, 66–71 (2004).
Lehtinen, T., Sundholm, G., Holmberg, S., Sundholm, F., Björnbom, P. & Bursell, M. Electrochemical characterization of PVDF-based proton conducting membranes for fuel cells. Electrochim. Acta 43, 1881–1890 (1998).
Dutta, K. & Kundu, P. P. Amphiphiles as hydrophobicity regulator: fine tuning the surface hydrophobicity of an electropolymerized film. J. Colloid Interface Sci. 397, 192–198 (2013).
Dutta, K. & Kundu, P. P. Interaction between oxidized polyaniline and oppositely charged amphiphilic assemblies in an aqueous/organic biphasic system. J. Colloid Interface Sci. 407, 516–523 (2013).
Dutta, K. & Kundu, P. P. Reversible assembly and disassembly of amphiphilic assemblies by electropolymerized polyaniline films: effects rendered by varying the electropolymerization potential. J. Phys. Chem. B 117, 7797–7805 (2013).
Dutta, K., Kumar, P., Das, S. & Kundu, P. P. Effects of various factors on the interfacial mass transfer phenomenon and dispersion of polyaniline in an aqueous/organic bi-/tri-phasic system. Colloids Surf. A Physicochem. Eng. Aspects 436, 830–838 (2013).
Dutta, K., Das, S., Rana, D. & Kundu, P. P. Enhancements of catalyst distribution and functioning upon utilization of conducting polymers as supporting matrices in DMFCs: a review. Polym. Rev. 55, 1–56 (2015).
Dutta, K. & Kundu, P. P. A review of aromatic conducting polymers-based catalyst supporting matrices for application in microbial fuel cells. Polym. Rev. 54, 401–435 (2014).
Pei, H., Hong, L. & Lee, J. Y. Effects of polyaniline chain structures on proton conduction in a PEM host matrix. J. Membr. Sci. 307, 126–135 (2008).
Yang, Z., Coutinho, D. H., Sulfstede, R., Balkus, K. J. Jr . & Ferraris, J. P. Proton conductivity of acid-doped meta- polyaniline. J. Membr. Sci. 313, 86–90 (2008).
Cho, K.-Y., Jung, H.-Y., Choi, N.-S., Sung, S.-J., Park, J.-K., Choi, J.-H. & Sung, Y.-E. A coated Nafion membrane with a PVdF copolymer/Nafion blend for direct methanol fuel cells (DMFCs). Solid State Ionics 176, 3027–3030 (2005).
Ramya, K. & Dhathathreyan, K. S. Direct methanol fuel cells: Determination of fuel crossover in a polymer electrolyte membrane. J. Electroanal. Chem. 542, 109–115 (2003).
Huang, Q. M., Zhang, Q. L., Huang, H. L., Li, W. S., Huang, Y. J. & Luo, J. L. Methanol permeability and proton conductivity of Nafion membranes modified electrochemically with polyaniline. J. Power Sources 184, 338–343 (2008).
Chen, C.-Y., Garnica-Rodriguez, J. I., Duke, M. C., Costa, R. F. D., Dicks, A. L. & da Costa, J. C. D. Nafion/polyaniline/silica composite membranes for direct methanol fuel cell application. J. Power Sources 166, 324–330 (2007).
Acknowledgements
KD thanks the Council of Scientific and Industrial Research (CSIR), India for a Senior Research Fellowship (Award no. 09/028 (0901)/2012-EMR-I). PPK thanks the Ministry of New and Renewable Energy (MNRE), Government of India for a Grant-in-Aid (Grant no. 102/56/2009-NT). We thank Mr Sujoy Debnath (University of Calcutta) for carrying out the tensile testing of the membranes.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Competing interests
The authors declare no conflict of interest.
Additional information
Supplementary Information accompanies the paper on Polymer Journal website
Supplementary information
Rights and permissions
About this article
Cite this article
Dutta, K., Das, S. & Kundu, P. Effect of the presence of partially sulfonated polyaniline on the proton and methanol transport behavior of partially sulfonated PVdF membrane. Polym J 48, 301–309 (2016). https://doi.org/10.1038/pj.2015.106
Received:
Revised:
Accepted:
Published:
Issue date:
DOI: https://doi.org/10.1038/pj.2015.106
This article is cited by
-
Development of novel proton exchange membranes based on cross-linked polyvinyl alcohol (PVA)/5-sulfosalicylic acid (SSCA) for fuel cell applications
Discover Applied Sciences (2024)
-
Novel sulfonated poly (vinyl alcohol)/carboxy methyl cellulose/acrylamide-based hybrid polyelectrolyte membranes
Scientific Reports (2022)
-
Preparation and characterization of the SPEEK/PVA/Silica hybrid membrane for direct methanol fuel cell (DMFC)
Polymer Bulletin (2022)
-
Chitosan/partially sulfonated poly(vinylidene fluoride) blends as polymer electrolyte membranes for direct methanol fuel cell applications
Cellulose (2018)