Table 1 Comparison of long-term cycle stability with reported ASSBs with areal capacity higher than 1 mAh cm−2
Positive electrode | Negative electrode | Electrolyte/ thickness (µm) | Areal capacity (mAh cm−2) | Current density (mA cm−2) | Cycle number | Stack Pressure (MPa) | Temperature (°C) | Ref. |
|---|---|---|---|---|---|---|---|---|
NMC811 | NTWO | LPSCl/ 500 | 2.96 | 14.85 | 100 | 60 | 60 | This work |
NMC811 | NTWO | LPSCl/ 500 | 1.8 | 18.75 | 1000 | 60 | 60 | This work |
NMC811 | NTWO | LPSCl/ 500 | 1.14 | 45 | 5000 | 60 | 60 | This work |
NMC811 | NTWO | LPSCl/ 500 | 1.09 | 101.66 | 2000 | 60 | 80 | This work |
NMC811 | Mg16Bi84/Li | LPSCl/ 500 | 2.5 | 15.3 | 300 | 2.5 | 80 | |
NMC811 | μ-Si | LPSCl/ 500 | 2 | 5 | 500 | 50 | 25 | |
NMC811 | LiSiH | LPSCl/ 650 | 3.6 | 5.86 | 5000 | 120 | 55 | |
LCO | Li-In | Li2In1/3Sc1/3Cl4/ 500a | 4.1 | 1.2 | 500 | 250 | 50 | |
NMC90 | Ag–C | LPSCl/ 40 | 4.6 | 3.4 | 1000 | 4 | 60 | |
SeSx | Li | LGPS-LPS bilayer/ 400a | 1.7 | 0.08 | 100 | 100 | 60 | |
NMC532 | Li | LPSCl/ 30 | 1.4 | 0.085 | 150 | 30 | 60 | |
NMC90 | SiC | LPSCl/ 750 | 2.3 | 0.2 | 50 | 100a | 25 | |
NMC622 | LTO | Li6.6P0.4Ge0.6S5I/ 450 | 3.4 | 1.71 | 50 | 265 | 60 |