Abstract
This study describes a simple, high-yield, rapid, and inexpensive route for the synthesis of cubic shape-like cerium oxide nanocubes (CeO2 NCs) using different urea concentrations (0.5, 1.0, and 2.0 g) by the hydrothermal method. The synthesized nanocubes (NCs) are labeled as CeO2 NCs-0.5, CeO2 NCs-1.0, and CeO2 NCs-2.0, corresponding to 0.5, 1.0, and 2.0 g of urea, respectively. The synthesized NCs were characterized by FT-IR, UV-visible, XRD, XPS, SEM and HR-TEM analysis. The synthesized NCs were cubic in shape with average sizes of 12, 12, and 13 nm for the CeO2 NCs-0.5, CeO2 NCs-1.0, and CeO2 NCs-2.0, respectively, obtained by the XRD analysis. The catalytic activity of the CeO2 NCs was studied for the purpose of obtaining the reduction of malachite green (MG) in the presence of sodium borohydride (NaBH4) at room temperature.
Similar content being viewed by others
Introduction
Environmental pollution is one of the most serious problems facing human beings and other life forms due to the increasing population, industrialization, and urbanization1. Dyes are major pollutants that are released from textile industrial effluent2. Malachite green (MG, including aniline green; basic green 4; diamond green B; and victoria green B) is a water-soluble cationic dye that is available in two forms malachite green chloride (C23H25ClN2) and malachite green oxalate (C52H54N4O12) (Table 1). It is used as an industrial dye for the dyeing of leather, wool, silk, cotton, jute, paper and the manufacturing of printing inks and paints3. The extensive usage of MG dye has caused several health problems, including significant effects on the immune and reproductive systems4. MG also has the potential to cause genotoxic and carcinogenic effects and is extremely cytotoxic to mammalian cells5, and hence the suitable treatment of wastewater containing MG dye is highly necessary. Several methods have been developed, such as physical, chemical, biological, and photocatalytic degradation methods for the treatment of industrial effluent3,6,7,8,9. The physical and chemical methods include adsorption10, ion-exchange11, irradiation12, oxidation processing13, chemical precipitation14, photolysis15, coagulation/flocculation16, electrochemical treatment17, ozonisation18, photo-Fenton degradation19,20, reduction and oxidation21. The biological methods include fungal degradation22, bacterial degradation23, and aerobic and anaerobic degradation24. However, these methods are generally expensive, are unable to completely remove the dye, and produce high sludge and by-products that cause secondary pollution25. In recent years photocatalytic degradation of organic dyes has been used effectively, but this process is slow and energy-consuming. Compared with photocatalytic activity, a catalytic reduction is a relatively fast process without high energy requirements26.
Ce is a rare earth element with a wide bandgap (~3.2 eV), lanthanide series, and exists as a free metal or oscillates between in the Ce3+ and Ce4+ oxidation states27. CeO2 NCs, also known as nanoceria, have been widely used in catalysis, fast-ion conductors, UV blockers, energy storage, and optical sensors due to its excellent physical and chemical properties28,29,30,31.
CeO2 is an effective catalyst for the removal of organic dyes from effluents because ceria also hops between Ce3+ and Ce4+ valence states containing oxygen vacancies that allow NCs to act as regenerative catalysts32. Various methods have been reported in the literature for the synthesis of ceria33,34,35,36,37, including sol-gel38, microwave combustion39, flame spray pyrolysis40, solvothermal41, microemulsion42, spray drying system43, hydrothermal44, and thermal decomposition45. Among these, the hydrothermal method is simple, which can produce high product yields46.
In this study we synthesized CeO2 NCs using urea (CH4N2O), as capping and reducing agent, urea was also known as carbamide and it is easily soluble in water. It has been used as a nitrogen source for the synthesis of environmentally benign nanoparticles. It has been widely used in many industries such as in agriculture, plastic, drug, soap, and detergent industries. However, excess concentrations urea in soil or in water causes to soil acidification and eutrophication and toxic effects to aquatic organisms, animals and humans47,48. The ceria nanocubes (CeO2 NCs) were synthesized via the one-pot hydrothermal method using different concentrations of urea. The CeO2 NCs are applied as a catalyst for the degradation of MG in the presence of NaBH4 in an aqueous medium using UV-visible spectroscopy.
Materials and Methods
Materials
Analytical grade cerium nitrate hexahydrate and urea were purchased from Alfa-Aesar, South Korea and used directly. Malachite green dye was obtained from Daejung Chemicals, South Korea. Deionized (DI) water was used throughout the study for the synthesis of CeO2 NCs and dye degradation studies.
Synthesis of ceria nanocubes
Cerium nitrate hexahydrate, 0.01 M was prepared at a volume of 70 mL in DI water. Different quantities of urea (0.5, 1.0 and 2.0 g) were added and stirred until dissolved. This reaction mixture was transferred to an autoclave at a temperature of 180 °C for 6 h. The reaction solution was naturally cooled down to room temperature. The reaction mixture was carefully collected by centrifuge and wished with DI and ethanol to remove the unreacted substance, before drying at 80 °C overnight. This was later calcined at 400 °C for 4 h and for comparison we prepared ceria without urea (CeO2 NCs-0.0).
Characterization
The crystallinity was measured by an X-ray diffractometer (PANalytical X-Pert PRO, USA) using a Cu Kα source (λ = 1.5405 Å). FT-IR (Perkin-Elmer, Bruker) was used to identify the vibrational modes by an ATR mode. The morphology of the samples was investigated by scanning electron microscopy (SEM-4800, Hitachi) and high-resolution transmission electron microscopy (TEM, Titan G2 ChemiSTM Cs Probe) with a 200 kV field emission gun in high brightness Schottky mode FEG (X-FEG). UV-visible absorption was measured on a Neogen (NEO-D3117). The elemental composition was quantitatively compared using an X-ray photoelectron spectrometer (K-alpha, Thermo Scientific, USA) with Al Kα radiation (1486.6 eV).
Catalytic activity
The synthesized samples were used to check the catalytic ability using the MG dye. For the catalytic reactions, 2.5 mL of the MG dye, 25 µL of well-dispersed CeO2 NCs (2 mg/mL) and 0.2 mL of (0.2 M) freshly prepared NaBH4 were added to all the samples. The degradation efficiency was monitored by UV-visible spectroscopy (Neogen, NEO-D3117). The degradation efficiency was calculated as a function of time for Co/Ct and ln Co/Ct, where Co is initial concentration and Ct is the final concentration of the MG dye. Blank control experiments were performed without catalyst (MG + NaBH4) or NaBH4 (MG + CeO2 NCs) to study the catalyst efficiency.
Results and Discussion
Characterization
The UV-visible absorbance spectra of the ceria nanocubes are shown in Fig. 1. The synthesized ceria nanocubes exhibited broad absorption peaks below 400 nm. Couple of broad absorption peaks were observed at wavelengths 208 and 311 nm (CeO2 NCs-0.5); 209 and 310 nm (CeO2 NCs-1.0); and 209 and 314 nm (CeO2 NCs-2.0). These peaks correspond to the characteristic absorption peaks of Ce3+ and Ce4+ of the CeO2 NCs. These results are similar to those obtained by Nurhasanah49 et al. who observed absorption peaks at 207 and 303 nm for CeO2 NCs (9 nm, precipitation method).
Fig. 2 shows the FT-IR spectra of the as-synthesized urea-based ceria nanocubes (CeO2 NCs-0.5, CeO2 NCs-1.0, and CeO2 NCs-2.0). The features near 1540 and 1630 cm−1 related to (ν C=O) and (N-H stretching) bond stretch50,51. The remaining observed peaks are as follows: near 3362 cm−1 (O-H stretching vibrations)52; near 2980 cm−1 (asymmetric C-H stretching)53; sharp band near 1340 cm−1 (N-O stretch due to the presence of nitrate)54; 1071 cm−1 (C-O stretching vibration)55; 850 cm−1 (formed by CeO2, which is typical peak of the Ce-O stretching vibrations)56; and below 700 cm−1 (O-Ce-O stretching vibrations)57.
Fig. 3 shows the XRD patterns of urea-based 0.5, 1.0 and 2.0 CeO2 NCs. The XRD revealed sharp peaks which located at 2θ = 28.5°, 32.9°, 47.5°, 56.3°, 59.0°, 69.3°, 76.7°, 78.8°, and 88.4°, are corresponding to (111), (200), (220), (311), (222), (400), (331), (420) and (422) planes, respectively. No extra peaks were observed, which supported the assumption that urea-based NCs are pure with cubic fluorite structure (JCPDC: 034–0394), similar peaks were also observed in CeO2 NCs-0.0 and results are shown in Fig. S1. The average mean grain size (MGS) of the NCs was calculated by the Debye- Scherer equation as follows58,59:
where β is the broadening in the full-width at half maximum (FWHM), λ is the X-ray wavelength (1.5406 Å), and θ is the Bragg diffraction angle. The microstrain, ε, of the NCs is evaluated by
The dislocation density δ, of the NCs is defined as the length of dislocations lines per unit volume and given by
The lattice strain (LS) of the NCs was calculated using the following relation60,61.
From Table 2, the MGS increased with the increasing urea concentration, for CeO2 NCs-0.5 and CeO2 NCs-1.0 were showing similar value (12 nm), and for CeO2 NCs-2.0 showing slightly bigger size (13 nm), whereas CeO2 NCs-0.0 showing much higher than (31 nm) urea mediated CeO2 NCs, this MGS analysis clearly indicating the urea was acted as capping and reducing agent to control the size of the NCs, meanwhile, the dislocation density decreased with increasing urea concentration, but for higher concentrations (CeO2 NCs-1.0 and CeO2 NCs-2.0) dislocation density was constant, in CeO2 NCs-0.0 too low than the urea mediated CeO2 NCs. The microstrain was constant with increasing urea concertation but without urea CeO2 NCs showing lower than other CeO2 NCs, however, lattice strain (LS) was constant for the first two concentrations (CeO2 NCs-0.5 and CeO2 NCs-1.0), and for the higher concertation (CeO2 NCs-2.0), it was slightly lowered compared with those of the lower concentrations, whereas in CeO2 NCs-0.0 showing very lower values, based on these results urea playing vital role as capping and reducing agent in the formation of CeO2 NCs.
To identify the chemical composition on the surface of the CeO2 NCs, we performed the XPS analysis (XPS analysis only for CeO2 NCs-0.5) and the results are presented in Fig. 4. The survey scan (Fig. S2(a)) clearly shows the presence of Ce and O elements. The high-resolution XPS spectrum of Ce shown in Fig. 4a contains six peaks, revealing that the Ce contained both the Ce3+ and Ce4+ oxidation states. The binding energies (BE) at 882.9, 901.2 and 917.2 eV are attributed to Ce4+, and the peaks at 885.5, 899.1 and 908.3 eV are the characteristic peaks of Ce3+. These results suggest the presence of mixed oxidations and a valence state for the Ce ions in the NCs62,63 and Deshpande64 et al. reported that Ce3+ ions create oxygen vacancies in the CeO2 lattice that are defects. There were three peaks in the high-resolution O 1 s deconvoluted spectrum in Fig. 4b; the O1 peak, O2 peak, and O3 peak, with 529.8, 532.0, and 533.6 eV binding energies, respectively. The O1 peak (529.8 eV) corresponds to the bond Ce-O, O2 peak (532.0 eV) is attributed to the oxygen vacancies, and O3 peak (533.6 eV) belongs to organic C=O bond or surface –OH groups. To get more information we performed XPS analysis for N 1 s, but the results are not showing any significant peak for N 1 s and results are shown in Fig. S2(b). These results are indicating the urea was acting as capping and reduction the formation of CeO2 NCs, not doped in CeO2 NCs, which are similar to the values in literature62,65,66,67.
The morphology of CeO2 NCs was obtained by SEM, and the images are revealed in Fig. 5. For CeO2 NCs-0.5, CeO2 NCs-1.0, and CeO2 NCs-2.0, SEM images show that aggregates were formed by the accumulation of nanocubes. SEM images of CeO2 NCs-0.0 was shown in Fig. S3, the results are indicating that the CeO2 NCs-0.0 were more in aggregation and size also higher than the urea mediated CeO2 NCs. The details of CeO2 NCs were further confirmed by HR-TEM studies. Fig. 6 shows the HR-TEM images of CeO2 NCs synthesized with different concentrations of urea. The TEM images show that CeO2 NCs were well dispersed, almost polydispersed, consisting of cubic shapes. The CeO2 NCs obtained with 0.5 urea-based NCs were smaller in size and less aggregated compared with the 1.0 and 2.0 urea-based NCs. To confirm the phase formation of the NCs, HR-TEM images were analyzed using the Gatan software, and the results are shown in Fig. 6a-iv–c-iv for CeO2 NCs-0.5, CeO2 NCs-1.0, and CeO2 NCs-2.0, respectively. The lattice fringe distance values were similar, 0.307 nm for CeO2 NCs-0.5, 0.307 nm for CeO2 NCs-1.0 and 0.306 nm CeO2 NCs-2.0, and were assigned to the (111) plane of the CeO2 NCs. The corresponding selected area electron diffraction (SAED) pattern (Fig. 6a–v, b–v and c–v for CeO2 NCs-0.5, CeO2 NCs-1.0, and CeO2 NCs-2.0) shows well-defined diffraction rings that confirm the polycrystalline nature of CeO2 NCs. These results were in good agreement with the XRD results. Therefore, the HR-TEM images revealed a good crystalline nature of the urea assisted NCs.
HR-TEM images of the cerium oxide nanocubes as a function of urea concentrations. The (a) top, (b) middle, and (c) bottom panels correspond to CeO2 NCs-0.5, CeO2 NCs-1.0, and CeO2 NCs-2.0, respectively. The panels labeled i–iii show different magnifications. The respective panels labeled iv shows the d-spacing values and line profiles, and v correspond to the SAED patterns.
Catalytic activity
MG dye was selected as a model pollutant to examine the catalytic activity of CeO2 NCs in the presence of NaBH4 as the reducing agent under ambient conditions. The results are presented in Fig. 7a to c for CeO2 NCs-0.5, CeO2 NCs-1.0, and CeO2 NCs-2.0, respectively. Fig. 7d shows a comparison of the absorption spectra of the catalytically degraded MG after 21 min in the presences of catalyst and NaBH4. The MG maximum absorption peak intensity was at~617 nm. The intense green color of the MG dye solution slowly faded becoming colorless, during the catalytic dye degradation process. A plot of Co/Ct versus degradation, time is shown in Fig. 8a for all samples, where Co is initial concentration and Ct is concentration at time ‘t’.
Langmuir-Hinshelwood pseudo-first order kinetics was applied to determine the first-order rate constant for dye degradation using the following relation68:
where ‘k’ is the rate constant (min−1) of the dye degradation reaction, Co is the initial concentration and Ct is the concentration of the dye solution after time ‘t’ in minutes, respectively. The results are shown in Fig. 8b. To identify the role of catalyst, we performed two control experiments. In the first experiment we performed the reaction between NaBH4 + CeO2 NCs and in the second experiments, we performed the reaction between dye (MG) + NaBH4, respectively. In both these control experiments, there was no observed degradation, based on these control experimental results we confirmed that the catalyst (CeO2 NCs) playing a vital role in the dye decolorization, and when both the catalyst + NaBH4 were together, the degradation materialized rapidly; the results are shown in Fig. 7a. The CeO2 NCs-0.5 exhibited an excellent dye degradation ~90%, while the CeO2 NCs-1.0 and CeO2 NCs-2.0 exhibited ~70% MG dye degradation within 21 min. The possible mechanism of dye reduction by the catalyst is explained by the electron relay system. The NCs start the catalytic reduction by relaying electrons from the donor \(B{H}_{4}^{-}\) to the dye molecules (acceptor), where the catalyst (NCs) accepted electrons from nucleophilic \(B{H}_{4}^{-}\) ions and transferred them to electrophilic dyes. Saikia et al. described hydrogen species generated from \(B{H}_{4}^{-}\) ions attack the dye (MG) molecules after electron transfer to nanocubes26. This reaction leads to a reduction in the MG dye, which is generally leuco MG (colorless). The CeO2 nanocatalysts show slope of −0.127, −0.061 and −0.064 for CeO2 NCs-0.5, CeO2 NCs-1.0, and CeO2 NCs-2.0, respectively. The rate constants for dye degradation were 0.127 min−1, 0.061 min−1, and 0.064 min−1 for CeO2 NCs-0.5, CeO2 NCs-1.0, and CeO2 NCs-2.0, respectively (Fig. 8a,b). CeO2 NCs-0.5 exhibited the highest dye degradation due to their size and high dispersion. We evaluated the catalytic activity of the CeO2 NCs-0.0, the rate constant was 0.03 min−1, as shown in Fig. S3 and it has shown poor performance than CeO2 NCs-1.0 and 2.0 that of counterparts due to bigger size and aggregation of particles.
Conclusion
We developed cost-effective CeO2 NCs using carbamide by one-pot hydrothermal method. The HR-TEM images revealed the synthesized NCs was cubic in shape. XRD results show the synthesized nanoparticles MGS of 12, 12, 13 and 31 nm for CeO2 NCs-0.5, CeO2 NCs-1.0, CeO2 NCs-2.0 and CeO2 NCs-0.0, respectively. These results were indicating that urea acting as capping and reducing agent. The synthesized CeO2 NCs also acted as efficient catalysts in the degradation of the MG dye.
References
Muralikrishna, I. V. & Manchikam, V. Introduction, chapter one. Envi. Management 1–4 (2017).
Mondal, P., Baksi, S. & Bose, D. Study of environmental issues in textile industries and recent wastewater treatment technology. World Sci. Reports 61, 98–109 (2017).
Raval, N. P., Shah, P. U. & Shah, N. K. Malachite green a cationic dye and its removal from aqueous solution by adsorption. Appl. Water Sci. 7, 3407–3445 (2017).
Singh, A. K. & Nakate, U. N. Photocatalytic properties of microwave-synthesized TiO2 and ZnO nanoparticles using malachite green dye. J. Nanopart. 2013, 310809 (2013).
Panandiker, A., Fernandes, C. & Rao, K. V. K. The cytotoxic properties of malachite green are associated with the increased demethylase, aryl hydrocarbon hydroxylase and lipid peroxidation in primary cultures of Syrian hamster embryo cells. Cancer Lett. 67, 93–101 (1992).
Tahir, H., Hammed, U., Sulthan, M. & Jahanzeb, Q. Batch adsorption technique for the removal of malachite green and fast green dyes by using montmorillonite clay as adsorbent. African J. Biotechnol. 9, 8206–8214 (2010).
Makeswari, M. & Santhi, T. Removal of malachite green dye from aqueous solutions onto microwave assisted zinc chloride chemical activated epicarp of Ricinus communis. J. Water Resou. Prot. 5, 222–238 (2013).
Al-Jawhari, I. F. H. & Al-Mansor, K. J. Biological removal of malachite green and congo red by some filamentous Fungi. Int. J. Envi. Agri. Biotechnol. 2, 723–731 (2017).
Meena, S., Vaya, D. & Das, B. K. Photocatalytic degradation of malachite green dye by modified ZnO nanomaterial. Bull. Mater. Sci. 39, 1735–1743 (2016).
Kaykhaii, M., Sasani, M. & Margzari, S. Removal of dyes from the environment by adsorption process. Chem. Mat. Eng. 6, 31–35 (2018).
Suteu, D., Bilba, D. & Coseri, S. Macroporous polymeric ion exchangers as adsorbents for the removal of cationic dye basic blue 9 from aqueous solutions. J. Appl. Polym. Sci. 39620 (2014).
Manh, H. B., Ngoc, D. N. & Quoc, H. N. Effects of gamma irradiation on color removal from reactive red 24 aqueous solutions. Sci. Technol. Develop. 19, 38–43 (2016).
EI Nemr, A., Hassaan, M.A. & Madkour, F. F. Advanced oxidation process (AOP) for detoxification of acid red 17 dye solution and degradation mechanism. 5, 95–113 (2018).
Zhu, M. X., Lee, L., Wang, H. H. & Wang, Z. Removal of an anionic dye by adsorption/precipitation processes using alkaline white mud. J. Hazard. Mat. 149, 735–741 (2007).
Soltani, T. & Entezari, M. H. Photolysis and photocatalysis of methylene blue be ferrite bismuth nanoparticles under sunlight irradiation. J. Mol. Cat A: Chem. 377, 197–203 (2013).
Moghaddam, S. S., Alavi Moghaddam, M. R. & Arami, M. Coagulation/flocculation process for dye removal using sludge from water treatment plant: Optimization through response surface methodology. J. Hazard. Mat. 175, 651–657 (2010).
Jain, R., Sharma, N. & Radhapyari, K. Electrochemical treatment of pharmaceutical azo dye amaranth from waste water. J. Appl. Electrochem. 39, 577–582 (2009).
Sripiboon, S. & Suwannahong, K. Color removal by ozonation process in biological wastewater treatment from breweries. IOP. Conf. Series: Earth Environ. Sci. 167, 012010 (2018).
D Bin, j, Xiaoying, L., Xuan, X. & Yu Xin, Z. Double-shell Fe2O3 hollow box-like structure for enhanced photo-Fenton degradation of malachite green dye. J. Phys. Chem. 112, 209–215 (2018).
De Bin, J. et al. Facile synthesis of three-dimensional/manganese silicate anorodss composites for enhanced Fenton-like catalytic dye degradation of malachite green dye. J. Nanopart. Res. 20, 123 (2018).
Wang, A. M., Qu, J. H., Liu, H. J. & Lei, P. J. Dyes wastewater treatment by reduction-oxidation process in an electrochemical reactor packed with natural manganese mineral. J. Environ. Sci. 18, 17–22 (2006).
Zuleta-Correa, A., Merino-Restrepo, A., Jimenez-Correa, S. & Hormaza-Anaguano, A. Use of white rot fungi in the degradation of an azo dye from the textile industry. DYNA 83, 128–135 (2016).
Ali Khan, K. & Srivastava, S. Decolorization and degradation of textile dyes by bacterial isolates. Res. Environ. Life Sci. 7, 299–304 (2014).
Wilfred Sugumar, R. & Sadanandhan, S. Combined anaerobic-Aerobic bacterial degradation of dyes. E-J. Chem. 7, 739–744 (2010).
Selvakumar, S., Manivasagam, R. & Chinnappan, K. Biodegradation and decolourization of textile dye wastewater using Ganoderma lucidum. Biotech. 3, 71–79 (2013).
Saikia, P., Miah, A. T. & Das, P. P. Highly efficient catalytic reductive degradation of various organic dyes by Au/CeO2-TiO2 nano-hybrid. J. Chem. Sci. 129, 81–93 (2017).
Ravishankar, T. N., Ramakrishnappa, T., Nagaraju, G. & Rajanaika, H. Synthesis and characterization of CeO2 nanoparticles via solution combustion method for photocatalytic and antibacterial activity studies. Chem. Open 4, 146–154 (2015).
Lu, X. et al. Facile synthesis of free-standing CeO2 nanorods for photoelectron chemical applications. Chem. Comm. 46, 7721–7723 (2010).
Park, S. D., Vohs, J. M. & Gorte, R. J. Direct oxidation of hydrocarbons in a solid-oxide fuel cell. Nature 404, 265–267 (2000).
Xu, C. W. & Shen, P. K. Novel Pt/CeO2/C catalyst for electrooxidation of alcohols in alkaline media. Chem. Comm. 404, 2238–2239 (2004).
Goharshadi, E. K., Samiee, S. & Nancarrow, P. Fabrication of cerium oxide nanoparticles: Characterization and optical properties. J. Colloid Int. Sci. 356, 473–480 (2011).
Arnold, M. C., Badireedy, A. R., Wiesher, M. R., Giulia, R. T. & Meyer, J. N. Cerium oxide nanoparticles are more toxic than equimolar bulk cerium oxide in Caenorhabditis elegans. Arch. Environ. Contam. Toxicol. 65, 224–233 (2013).
McKerracher, R. D. et al. Improving the stability and discharge capacity of nanostructured Fe2O3/C anodes for iron-air batteries and investigation of 1-octhanethiol as an electrolyte additive. Electrochim. Acta 318, 625–634 (2019).
Diego, P. et al. Luminescent downshifting by photo-induced sol-gel hybrid coatings: Accessing multifunctionality on flexible organic photovoltaics via ambient temperature material processing. Adv. Electro. Mat. 2, 1600288 (2016).
Beatrice, M. et al. One-dimensional ZnO/gold junction for simultaneous and versatile multisensing measurements. Sci. Reports 6, 29763 (2016).
Federico, B. et al. Combined structural, chemometric, and electrochemical investigation of vertically aligned TiO2 nanotubes for Na-ion batteries. ACS Omega 3, 8440–8450 (2018).
Louis, L. P. et al. Spray-dried mesoporous mixed Cu-Ni oxide @graphene nanocomposite microspheres for high power and durable Li-ion battery anodes. Adv. Energy Mat. 8, 1802438 (2018).
Periyat, P., Laffir, F., Tofail, S. A. M. & Magner, E. A facile aqueous sol-gel method for high surface area nanocrystalline CeO2. RSC Adv. 1, 1794–1798 (2011).
Tamizidurai, P. et al. Environmentally friendly synthesis of CeO2 nanoparticles for the catalytic oxidation of benzyl alcohol to benzaldehyde and selective detection of nitrite. Sci. Reports 7, 46372 (2017).
Xiong, Z. et al. Flame spray pyrolysis synthesized ZnO/CeO2 nanocomposites for enhanced CO2 photocatalytic reduction under UV-Vis light irradiation. J. CO 2 Utili. 18, 53–61 (2017).
Kumar, E., Selvarajan, P. & Muthuraj, D. Synthesis and characterization of CeO2 nanocrystals by solvothermal route, Mat. Res. 16, 269–276 (2013).
Bumajdad, A., Zaki, M. I., Eastoe, J. & Lata, P. Microemulsion-based synthesis of CeO2 powders with high surface area and high-temperature stabilities. Langmuir 20, 1123–1133 (2004).
Sharma, V., Eberhardt, K. M., Sharma, R., Adams, J. B. & Crozier, P. A. A spray drying system for synthesis of rare-earth doped cerium oxide nanoparticles. Chem. Phys. Lett. 495, 280–286 (2010).
Tok, A. I. Y., Boey, F. Y. C., Dong, Z. & Sun, X. L. Hydrothermal synthesis of CeO2 nano-particles. J. Mat. Proc. Technol. 190, 217–222 (2007).
Miyazaki, H. et al. Synthesis of CeO2 nanoparticles by rapid thermal decomposition using microwave heating. Appli. Ceramics 109, 123–127 (2010).
Aneesh, P. M., Vanaja, K. A. & Jayaraj, M. K. Synthesis of ZnO nanoparticles by hydrothermal method. Proc. Of SPIE nanophotonic Mat. 6639, 66390 J (2007).
Vignesh Kumar, T. H. & Sundramoorthy, A. K. Non-enzymatic electrochemical detection of urea on silver nanoparticles anchored nitrogen-doped single-walled carbon nanotube modified electrode. J. Electrochem. Soc. 165, B3006–B3016 (2018).
Hilding-Ohlsson, A. Fauerbach, J.A. Sacco, N.J. Bonetto, M.C. & Corton, E. Voltamperometric discrimination of urea and melamine adulterated skimmed milk powder. Sensors (Basel), 12220-12234 (2012).
Nurhasanah, I., Safitri, W., Arifin, Z., Subagio, A. & Windarti, T. Antioxidant activity and dose enhancement factor of CeO2 nanoparticles synthesized by precipitation method. IOP. Conf. Series: Mat. Sci. Eng. 432, 012031 (2018).
Grdadolnik, J. & Marechal, Y. Urea and urea-water solutions-an infrared study. J. Mol. Stru. 615, 177–189 (2002).
Valério, A., Araújo, P. H. H. & Sayer, C. Preparation of poly (urethane-urea) nanoparticles containing açaí oil by miniemulsion polymerization. Polimeros 23, 451–455 (2013).
Zamiri, R. et al. Dielectrical properties of CeO2 nanoparticles at different temperatures. Plos one 10, e0131851 (2015).
Pujar, M. S., Hunagund, S. M., Desai, V. R., Patil, S. & Sidarai, A. H. One-step synthesis and characterization of cerium oxide nanoparticles in an ambient temperature via co-precipitation method. AIP. Conf. Proc. 1942, 050026 (2018).
Chelliah, M., Rayappan, J. B. B. & Krishnan, U. M. Synthesis and characterization of cerium oxide nanoparticles by hydroxide mediated approach. J. Appli. Sci. 12, 1734–1737 (2012).
Farahmandjou, M., Zarinkamar, M. & Firrozabadi, T. P. Synthesis of cerium oxide (CeO2) nanoparticles using simple co-precipitation method. Revista Mexicana de Fisica 62, 496–499 (2016).
Babitha, B. K., Sreedevi, A., Priyanka, K. P., Sabu, N. & Varghese, T. Structural characterization and optical studies of CeO2 nanoparticles synthesized by chemical precipitation. Indian J. Pure Appli. Phys. 53, 596–603 (2015).
Prabaharan, D. M. D. M., Sadaiyandi, K., Mahendran, M. & Sagadevan, S. Structural, optical, morphological and dielectric properties of cerium oxide nanoparticles. Mat. Res. 19, 478–482 (2016).
Sreekanth, T. V. M. et al. Doo Hwan Kim, Jaesool Shim & Kisoo Yoo. Ultra-sonication-assisted silver nanoparticles using Panax ginseng root extract and their anti-cancer and antiviral activities. J. Photochem. Photobiol. B: Biol. 188, 6–11 (2018).
Nagaraju, P., Vijayakumar, Y., Phase, D. M., Reddy, V. R. & Ramana Reddy, M. V. Preparation and microstructural characterization of Si(100) Ce1−xGdxO2−δ thin films prepared by pulsed laser deposition technique. Mat. Sci. Poland 32, 541–546 (2014).
Govindarajan, D. & Nithya, C. K. Structural and optical properties of cerium oxide thin films prepared by Spray Pyrolysis technique. Int. J. Sci. Eng. Res. 5, 427–430 (2014).
Nagajyothi, P. C., Devarayapalli, K. C., Tettey, C. O., Prabhakar Vattikuti, S. V. & Jaesool, S. Eco-friendly green synthesis: catalytic activity of nickel hydroxide nanoparticles. Mat. Res. Exp. 6, 055036 (2019).
Yeng, Y., Jin, Y., He, H. & Ye, Z. Facile synthesis and characterization of ultrathin cerium oxide nanorods. Cryst. Eng. Comm. 12, 2663–2665 (2010).
Kar, S., Patel, C. & Santra, S. Direct room temperature synthesis of valence state engineered ultra-small ceria nanoparticles: Investigation on the role of ethylenediamine as a capping agent. J. Phys. Chem. C 113, 4862–4867 (2009).
Deshpande, S., Patil, S., Kuchibhatla, S. & Seal, S. Size dependency variation in lattice parameter and valency states in nanocrystalline cerium oxide. Appl. Phys. Lett. 87, 133113 (2005).
Yu, R., Yan, L., Zheng, P., Chen, J. & Xing, X. Controlled synthesis of CeO2 flower-like and well-aligned anorods hierarchical architectures by a phosphate-assisted hydrothermal route. J. Phys. Chem. C 112, 19896–19900 (2008).
Sreekanth, T. V. M., Nagajyothi, P. C., Dillip, G. R. & Lee, Y. R. Determination of band alignment in the synergistic catalyst of electron structure modified graphitic carbon nitride-integrated ceria-quantum dots hetero junction for rapid degradation of organic pollutants. J. Phys. Chem. C 121, 25229–25242 (2017).
Talha, A. et al. I. Morphology engineering of self-assembled nanostructured CuCo2O4 anodes for lithium-ion batteries. Energy Technol. 7, 1900295 (2019).
Dillip, G. R., Sreekanth, T. V. M. & Joo, S. W. Tailoring the bandgap of N-rich graphitic carbon nitride for enhanced photocatalytic activity. Ceram. Int. 43, 6437–6445 (2017).
Acknowledgements
This work was supported by the National Research Foundation of Korea (NRF) grant funded by the Korean government (NRF-2017R1C1B2001990) and 2017 Yeungnam University Research Grant.
Author information
Authors and Affiliations
Contributions
The manuscript was written through the contributions of all authors. T.V.M.S.K., P.C.N.J. and G.R.R. conducted the synthesis, characterization, and application. J.S. and K.Y. designed and supervised the project.
Corresponding author
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Sreekanth, T.V.M., Nagajyothi, P.C., Reddy, G.R. et al. Urea assisted ceria nanocubes for efficient removal of malachite green organic dye from aqueous system. Sci Rep 9, 14477 (2019). https://doi.org/10.1038/s41598-019-50984-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-019-50984-6
This article is cited by
-
Degradation of malachite green by g-C3N4-modified magnetic attapulgite composites under visible-light conditions
Environmental Science and Pollution Research (2023)
-
Highly dispersed and ultra-small Ni nanoparticles over hydroxyapatite for hydrogenation of levulinic acid
Reaction Kinetics, Mechanisms and Catalysis (2022)
-
Application of Taguchi method and response surface methodology into the removal of malachite green and auramine-O by NaX nanozeolites
Scientific Reports (2021)