Table 1 Results of five experiments for each launching condition.
U/V | Sa /µm | ‾Sa /µm | Sz /µm | ‾Sz /µm | U/V | Sa /µm | ‾Sa /µm | Sz /µm | ‾Sz /µm | |
|---|---|---|---|---|---|---|---|---|---|---|
Different charging voltages | 1900 | 9.79 | 9.82 | 552.89 | 552.99 | 2000 | 8.18 | 8.18 | 511.95 | 511.93 |
9.82 | 553.04 | 8.12 | 511.81 | |||||||
9.83 | 552.99 | 8.15 | 511.96 | |||||||
9.88 | 553.08 | 8.21 | 511.88 | |||||||
9.81 | 552.94 | 8.24 | 512.06 | |||||||
2100 | 8.41 | 8.46 | 491.59 | 491.68 | 2200 | 8.36 | 8.35 | 437.08 | 437.07 | |
8.43 | 491.62 | 8.29 | 436.99 | |||||||
8.46 | 491.73 | 8.32 | 437.02 | |||||||
8.49 | 491.69 | 8.37 | 437.11 | |||||||
8.53 | 491.78 | 8.41 | 437.18 | |||||||
2300 | 7.99 | 7.99 | 414.26 | 414.23 | 2400 | 7.76 | 7.82 | 367.18 | 367.28 | |
7.96 | 414.19 | 7.80 | 367.28 | |||||||
8.06 | 414.32 | 7.85 | 367.32 | |||||||
8.02 | 414.24 | 7.89 | 367.34 | |||||||
7.92 | 414.11 | 7.81 | 367.24 | |||||||
Sa0 /µm | Sa /µm | ‾Sa /µm | Sz /µm | ‾Sz /µm | Sa0 /µm | Sa /µm | ‾Sa /µm | Sz /µm | ‾Sz /µm | |
Different initial roughness | 2.65 | 7.72 | 7.74 | 527.31 | 527.34 | 2.15 | 7.43 | 7.43 | 499.39 | 499.41 |
7.76 | 527.33 | 7.45 | 499.41 | |||||||
7.66 | 527.23 | 7.41 | 499.43 | |||||||
7.74 | 527.38 | 7.49 | 499.51 | |||||||
7.79 | 527.43 | 7.36 | 499.35 | |||||||
1.65 | 7.23 | 7.31 | 483.66 | 483.84 | 1.05 | 7.93 | 7.91 | 498.30 | 498.31 | |
7.32 | 483.81 | 7.81 | 498.22 | |||||||
7.29 | 483.82 | 7.99 | 498.41 | |||||||
7.36 | 483.93 | 7.92 | 498.36 | |||||||
7.33 | 483.89 | 7.88 | 498.27 | |||||||
0.55 | 8.36 | 8.31 | 515.09 | 514.91 | 0.25 | 8.86 | 8.88 | 544.43 | 544.44 | |
8.31 | 514.91 | 8.88 | 544.46 | |||||||
8.23 | 514.83 | 8.96 | 544.56 | |||||||
8.33 | 514.95 | 8.68 | 544.35 | |||||||
8.29 | 514.87 | 8.90 | 544.43 | |||||||
0.15 | 9.66 | 9.58 | 577.38 | 577.25 | 0.05 | 10.66 | 10.68 | 616.13 | 616.09 | |
9.56 | 577.24 | 10.61 | 616.00 | |||||||
9.57 | 577.23 | 10.71 | 616.08 | |||||||
9.61 | 577.28 | 10.76 | 616.19 | |||||||
9.49 | 577.17 | 10.67 | 616.06 |