Table 3 Oxidative weight gain rate constants at different temperatures (mg2·cm− 4·min− 1).
From: Ironmaking and steelmaking process research on Chinese long ring pommel Dao in Han dynasty
Si% | 600 | 700 | 800 | 900 | 1000 | 1050 | 1100 | 1150 |
|---|---|---|---|---|---|---|---|---|
0.35 | – | – | – | – | 14.4 | – | – | 14.4 |
0.75 | 7.01 × 10− 4 | 2.64 × 10− 3 | 2.91 × 10− 3 | 3.88 × 10− 3 | 1.96 × 10− 1 | 7.91 × 10− 1 | 15.8 | 16 |
1.5 | 6.52 × 10− 4 | 2.28 × 10− 3 | 2.29 × 10− 3 | 4.16 × 10− 3 | 1.48 × 10− 1 | 6.28 × 10− 1 | 14.2 | 29.8 |
2.2 | 4.01 × 10− 4 | 2.32 × 10− 3 | 2.70 × 10− 3 | 4.38 × 10− 3 | 4.51 × 10− 3 | 5.07 × 10− 2 | 0.579 | 17.2 |