Fig. 6: External field dependence of magnetization.
From: Organic magnetoelectric and optomagnetic couplings: perspectives for organic spin optoelectronics
a Room-temperature magnetoelectric character of P3HT nanowire:C60; the magnetization could be switched by a very small voltage. The electric field of the film sample was created parallel to the normal of the film, whereas the magnetic field was applied perpendicular to it. The measurements were performed in the dark. b Room-temperature magnetoelastic character of P3HT nanowire:C60; the (dark) magnetization could be switched by very small negative and positive strains. The magnetoelastic response should be antisymmetric. Reproduced from Ren and Wutting62 with permission from Wiley-VCH.