Table 3 Fitted rate model parametersa, number of observations, R2, and parameter correlation coefficients for the data set used in this study

From: Impacts of glass composition, pH, and temperature on glass forward dissolution rate

Glass

Fit parameters

Parameter correlations

ID

log[k0]

η

Ea, kJ mol−1

Obs

R 2

RMSE

Ea−log[k0]

η−log[k0]

η−Ea

AFCI

8.327

0.510

89.52

15

0.985

0.135

0.810

−0.1253

0.4767

EWG-C

7.619

0.297

72.86

17

0.969

0.186

0.844

−0.397

0.1514

IDF18-A161

7.149

0.283

63.66

13

0.946

0.158

0.849

0.1159

0.6206

IDF1-B2

6.135

0.493

74.76

19

0.983

0.146

0.832

−0.421

0.1477

IDF21-EC14

6.195

0.492

75.81

17

0.993

0.092

0.809

−0.3079

0.3055

IDF7-E12

5.824

0.322

62.73

17

0.980

0.119

0.807

−0.2662

0.3496

ISG

8.367

0.396

81.55

15

0.983

0.141

0.800

−0.2255

0.3993

LAW-A44

6.224

0.437

71.34

16

0.953

0.215

0.839

−0.2553

0.307

LAW-ABP1

6.753

0.325

68.06

12

0.994

0.081

0.886

−0.3635

0.1043

LAW-B45

5.995

0.362

66.91

17

0.975

0.145

0.860

−0.2634

0.2617

LAW-C22

6.733

0.324

68.19

15

0.981

0.115

0.804

−0.1285

0.4822

LD6-5412

6.962

0.381

73.53

18

0.983

0.138

0.824

−0.2876

0.3005

MT25

9.422

0.476

88.23

9

0.973

0.205

0.923

−0.1669

0.2209

MT30

7.788

0.495

79.91

9

0.972

0.201

0.923

−0.1669

0.2209

ORLEC28

6.429

0.552

79.19

30

0.986

0.126

0.785

−0.3202

0.3308

ORLEC33

6.584

0.562

80.72

31

0.987

0.124

0.788

−0.3076

0.3386

ORPLG9

9.527

0.298

84.54

15

0.954

0.245

0.796

−0.3459

0.2879

SON68

8.524

0.389

82.90

15

0.978

0.168

0.782

−0.2948

0.3602

SRL-202

7.473

0.535

86.53

15

0.982

0.154

0.819

−0.192

0.4015

  1. aNote: These values differ in some cases compared to the originally reported values, primarily due to outlier removal, but potentially also due to differences in significant figures in reported values