Table 1 Nominal compositions (mol%) of the six glasses designed to investigate the influence of Al on aluminoborosilicate glass, glass densities calculated from Fluegel’s model56, and geometric surface area and BET surface area of the powders used in this study. For the rate calculation, the BET surface area was used.
From: On the effect of Al on alumino-borosilicate glass chemical durability
SiO2 | B2O3 | Na2O | Al2O3 | Density (g.cm3) | Sgeo 100–125 µm (cm2.g−1) | SBET 100–125 µm (cm2.g−1) | Sgeo 40–100 µm (cm2.g−1) | SBET 40–100 µm (cm2.g−1) | |
|---|---|---|---|---|---|---|---|---|---|
SBNA0 | 67.8 | 18 | 14.2 | 0 | 2.42 | 220 | 405 | 354 | 690 |
SBNA1 | 63 | 18.7 | 17.3 | 1 | 2.46 | 217 | 355 | 348 | 645 |
SBNA1bis | 60.5 | 20.1 | 18.4 | 1 | 2.46 | 217 | 415 | 348 | 720 |
SBNA3.5 | 60.5 | 20.1 | 15.9 | 3.5 | 2.40 | 222 | 415 | 357 | 715 |
SBNA4 | 64.9 | 17.3 | 13.7 | 4.1 | 2.39 | 223 | 435 | 359 | 720 |
SBNA6 | 66.8 | 15.9 | 11.3 | 6 | 2.36 | 226 | 455 | 363 | 780 |