Table 3 Chemical composition (in wt%) of model glass (of cited references).

^{37,98,102,125,126,178}

Si-K-Ca

50

2

25

18

3

2

100.0

⁸⁸

SG1

52

2.4

22.6

17.7

3.3

0.4

1.6

100.0

⁸⁸

SG2

54.7

2.2

20.6

15.6

3.5

3.4

100.0

^36,85,91,140

SG3

51.3

1.8

19.2

16.8

4

1

1.1

1.2

3.8

100.2

^{29,31,136,147}

M1 or MI

48

1.5

25.5

15

3

3

4

100.0

^31,131,136

M3

60

15

25

100.0

^128,179

Ca-K

53.67

0.83

18.77

21.57

3.3

1.53

99.7

¹²⁷

SC

53

1.7

18

15

5.8

1

1

4.4

99.9

¹²⁷

TR

51

2.3

24

16

3

0.8

0.5

0.5

1.9

100.0

¹²⁷

CL_I

50.5

1.8

20.2

19

3.9

1.5

0.5

0.5

1.8

99.7

¹²⁷

CL_II

46

3.5

11

30

4

0.5

0.5

0.8

3.7

100.0

³⁰

Potash-lime

60

15

25

100.0

¹⁰⁰

KCS

46.2

3.6

21.9

20.5

2.9

0.8

3.3

0.1

99.3

¹⁸⁰

KCV

57.14

4.16

17.56

16.64

1.96

0.1

0.12

1.76

0.06

0.48^a

100.0

^111,147

M1.0

54.2

28.8

17

100.0

¹⁴⁸

Glass 2

48.4

2.5

10.6

30.3

3.2

1.1

0.5

3.4

100.0

¹⁴⁸

Glass 3

47.2

2.4

16.3

26

3.2

1.1

0.5

3.3

100.0

¹⁴⁸

Glass 4

46.1

2.3

21.7

21.9

3.1

1.1

0.5

3.3

100.0

¹³¹

M I53.1

53.1

1

18

17.8

5

3.2

1.9

100.0

¹³¹

M 2.0

57.1

22.5

20.4

100.0

^65,132

VK

52.19

2.39

14.9

14.9

4.9

0.76

1.8

0.7

3.34

0.24

96.1

¹³³

GIC1

46.1

1.6

13.9

18.8

7.4

1.7

3

7

99.5

¹³⁴

4

47.33

3.34

18.81

22.65

3.22

1.02

0.7

0.06

2.87

100.0

^135,139

BMG

51

20.4

28.6

100.0

¹³⁷

Type 3

53.02

2.5

17.8

14.22

4.21

0.91

0.55

0.99

3.47

0.14

2.17^b

100.0

¹³⁸

V1

61.11

1.99

12.29

18.5

3.82

0.03

0.38

0.15

1.67

0.09

100.0

¹³⁸

V2

57.07

1.38

16.74

18.64

3.57

0.02

0.67

0.22

1.62

0.06

100.0

¹³⁸

V3

53.1

0.73

23.49

17.53

3.24

0.02

0.26

0.09

1.52

0.03

100.0

¹¹³

VM

51.5

1.8

18.3

17.3

4.3

2.0

1.2

3.2

99.6

¹¹³

VNM

52.4

1.9

18.8

17.6

4.3

1.2

3.4

99.6