Table 1 Mechanical properties of the constructs.

From: Parylene C topographic micropattern as a template for patterning PDMS and Polyacrylamide hydrogel

Material

hf [nm]

hmax [nm]

hf/hmax

Es

E

Parylene C

256.04 ± 18.4a

446.31 ± 89.4a

0.57a

4.35 ± 0.4a [GPa]

4.85[GPa]

PDMS

895.90 ± 93.4b

2815.84 ± 72.2b

0.33b

55.46 ± 1.9b [MPa]

22 [MPa]

Parylene C/PDMS

723.33 ± 184.4b

2818.25 ± 60.8b

0.26b

59.33 ± 2.4b [MPa]

47.3 [MPa]

  1. aValues for 0.9 mN. bValues for 1 mN.