Table 1 Yield strength \({\sigma }_{y}\), tensile strength \({\sigma }_{T}\), strength at the fracture of MG wire \({\sigma }_{f,w}\), strain at the fracture of MG wire \({\varepsilon }_{f,w}\), fracture strength \({\sigma }_{f}\), and fracture strain \({\varepsilon }_{f}\) of Cu-coated Pd40Cu30Ni10P20 MG wires with different R values.
From: Tensile behavior of Cu-coated Pd40Cu30Ni10P20 metallic glassy wire
R | \({\sigma }_{y}\) (MPa) | \({\sigma }_{T}\) (MPa) | \({\sigma }_{f,w}\) (MPa) | \({\varepsilon }_{f,w}\) (%) | \({\sigma }_{f}\) (MPa) | \({\varepsilon }_{f}\) (%) |
|---|---|---|---|---|---|---|
0% | 1633 ± 24 | 1633 ± 24 | 1633 ± 24 | 2.21 ± 0.322 | 1633 ± 24 | 2.21 ± 0.32 |
45% | 941 ± 17 | 941 ± 17 | 1198 ± 21 | 2.49 ± 0.34 | 1198 ± 21 | 2.49 ± 0.34 |
70% | 484 ± 16 | 900 ± 17 | 873 ± 14 | 2.55 ± 0.26 | 873 ± 15 | 2.55 ± 0.31 |
90% | 371 ± 10 | 588 ± 13 | 547 ± 13 | 3.82 ± 0.21 | 260 ± 11 | 3.98 ± 0.20 |
97% | 311 ± 9 | 498 ± 10 | 464 ± 9 | 7.09 ± 0.24 | 0 | 8.50 ± 0.18 |