Table 1 Output parameters of organic photovoltaic cells using ZnOHx inter-layer.

From: Thin Film of Amorphous Zinc Hydroxide Semiconductor for Optical Devices with an Energy-Efficient Beneficial Coating by Metal Organic Decomposition Process

Precursor conc.

100 mM/Lb

50 mM/Lb

30 mM/Lb

20 mM/Lb

10 mM/Lb

ZnOc

Thickness [nm]

60 ± 5

40 ± 3

20 ± 3

10 ± 3

<5

ca. 35 ± 5

Jsc [mA/cm2]

1.348

16.153

15.836

15.950

16.020

16.693

Voc [V]

0.645

0.728

0.725

0.748

0.716

0.733

FF

0.561

0.555

0.572

0.624

0.603

0.608

PCEa [%]

0.49(0.47)

6.52(6.04)

6.57(6.06)

7.44(7.25)

6.91(6.34)

7.44(7.26)

Forward voltage [V]

0.57

0.55

0.55

0.59

0.51

0.47

  1. aaveraged values on 10 devices in parentheses, bconcentration of precursors, cannealed at 300 °C for 5 min.