Figure 11
The time evolution of the SPS processing parameters for the sample prepared at 950 °C under the pressure 80 MPa for 1 min from the powders mixture CoNiAl:Ti in the ratio of 1:2. The 9 g of powder mixture was processed in a 20 mm wide die.