Figure 8
From: Effects of Precipitates Evolution on Low Stress Creep Properties in P92 Heat-resistant Steel
Creep rate εM curves of P92 heat-resistant steel specimens following thermal aging for different times at 923 K under stress of 20 MPa, 35 MPa, 65 MPa and 75 MPa.