Table 1 The cell parameter a, the average coherent diffraction domain length, <LXRD > and the weight content of each phase in the all analyzed ceramics, as inferred from MAUD refinements49 (see Figure SI-1 in the supporting information section).
CoFe2O4 | CoO | fcc-Co | hcp-Co | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|
a (Å) ± 0.002 | <LXRD > (nm) | Wt.-% | a (Å) ± 0.002 | <LXRD>nm | Wt.-% | a (Å) ± 0.002 | <LXRD > (nm) | Wt.-% | a (Å) ± 0.002 | <LXRD > (nm) | Wt.-% | |
CFO | 8.389 | 37 | 89 | — | — | — | 3.550 | 100(*) | 11 | — | — | — |
CFO-CO | 8.388 | 27 | 58 | 4.260 | 32 | 32 | 3.550 | 100(*) | 7 | 2.500 | 100(*) | 3 |
4.050 | ||||||||||||
CO | — | — | — | 4.260 | 37 | 95 | — | — | — | 2.500 | 100(*) | 5 |
4.050 | ||||||||||||