Figure 3
Log-log plot of in-situ small angle neutron scattering intensity measured over a Q-range of 0.02 to 0.3 Å−1 for the sintered sample continuously annealed from ambient temperature to 800 °C. Extremely low variation in intensity was observed below 500 °C and is not presented here.