Figure 1
From: Electronic transport properties of a lithium-decorated ZrTe5 thin film
Temperature dependence of resistance in various lithium adsorption processes. These data were measured after the deposition associated with each process (see Table 3) during the cooldown to 4 K. The resistance peak is initially at  ~130 K in the pristine sample. Upon the first heating cycle in process 4, the peak is now found at 122 K. The peak is not revisited until processes 7, and 9–11, where it is repeatedly found at 183 K despite further lithium adsorption and possible intercalation.