Figure 7 | Scientific Reports

Figure 7

From: New Synthesis Route for Complex Borides; Rapid Synthesis of Thermoelectric Yttrium Aluminoboride via Liquid-Phase Assisted Reactive Spark Plasma Sintering

Figure 7

Temperature dependence of logarithmic electrical conductivities of Al-poor (YA0-P) and -rich samples (YA1, YA2 and YA3) prepared by reactive SPS. The YA0-P sample was sintered at 1773 K for 5 min under 80 MPa, whereas the YA1, YA2 and YA3 samples were sintered at 1773 K for 60 min under ~30 MPa. Error bars represent a measurement uncertainty range (±7%).