From: Facile fabrication of solution-processed solid-electrolytes for high-energy-density all-solid-state-batteries by enhanced interfacial contact

Figure 6

Comparison of LPSCl distribution inside the electrodes using different sizes of active materials: either small (only 4 µm) and large (only 10 µm) particles or a mixture of two different sized particles. (a) Schematics of different size effects of active materials on a solution-based LPSCl infiltration process with the same loading value of ~ 17.5 mg/cm2. (b) FE-SEM images of NCM622-based composite electrodes with different active material sizes (left) 4 µm particles only, (middle) 10 µm particles only, and (right) a mixture of 4 and 10 µm particles.