Figure 3 | Scientific Reports

Figure 3

From: Evidence of disruption of Si-rich microstructure in engineering-lightweight Al–12.2at.%Si alloy melt above liquidus temperature

Figure 3

Cross-section SEM morphology of (a–d) Al–3at.%Si, (e–h) Al–7at.%Si, (i–l) Al–12.2at.%Si and (m–p) Al–20at.%Si melt-spinning alloy ribbons rapid solidified from melts at 1100 °C: (a, e, i, m) low magnification (×1 k) cross-section morphology, and high magnification (×30 k) morphology of Si particles (b, f, j, n) near the wheel side, (c, g, k, o) in the center, and (d, h, l, p) near the free surface of the melt-spinning alloy ribbons.

Back to article page