Table 3 The statistical analysis of wood mechanical properties of Chinese fir.

From: Variation in wood physical properties and effects of climate for different geographic sources of Chinese fir in subtropical area of China

Sources

MOE (MPa)

MOR (MPa)

TSG (MPa)

CSG (MPa)

FJYK-P

8639.42 ± 1375.67

63.09 ± 11.48

55.64 ± 14.94

32.60 ± 6.63

HNYX-P

11,870.34 ± 1791.81

89.85 ± 13.96

94.06 ± 22.59

48.92 ± 4.31

HNYX-T

10,587.36 ± 1699.75

93.34 ± 25.86

127.64 ± 38.98

56.33 ± 4.93

HNZJJ-P

9945.92 ± 1373.69

71.45 ± 18.58

78.90 ± 22.36

41.01 ± 7.49

JXCS-R

10,901.91 ± 1151.05

96.66 ± 7.41

105.39 ± 15.68

50.52 ± 4.02

  1. Data are means ± SE.
  2. MOE modulus of elasticity (MPa), MOR modulus of rupture (MPa), TSG tensile strength parallel to grain (MPa), CSG compression strength parallel to the grain (MPa).
Back to article page