Table 1 Fit parameters within the XPS analysis of asymmetric components, applied to the Ag 3d core-level signal in Fig. 1a.
From: Tracing the structural evolution of quasi-freestanding germanene on Ag(111)
Figure 1 | \(\Theta\) \((^{\circ })\) | Comp. | \(E_\mathrm {kin}\) \((\hbox {eV})\) | \(E_\mathrm {SOC}\) \((\hbox {eV})\) | \(\mathrm {FWHM}\) \((\hbox {eV})\) | \(\alpha\) | \(A_\mathrm {rel}\) \((\%)\) |
|---|---|---|---|---|---|---|---|
(a) | 0 | Ag | 107.61 | 6.00 | 0.78 | 0.02 | 98.7 |
P1 | 103.56 | 1.13 | 0.00 | 0.9 | |||
P2 | 97.55 | 1.12 | 0.00 | 0.4 | |||
60 | Ag | 107.61 | 6.00 | 0.78 | 0.02 | 98.1 | |
P1 | 103.56 | 1.13 | 0.00 | 1.1 | |||
P2 | 97.55 | 1.12 | 0.00 | 0.8 |