Table 3 Peak fit parameters of the Ag 3d signal resulting from the XPS analysis shown in Fig. 5.
From: Tracing the structural evolution of quasi-freestanding germanene on Ag(111)
Figure 5 | \(\Theta\) \((^{\circ })\) | comp. | \(E_\mathrm {kin}\) \((\hbox {eV})\) | \(E_\mathrm {SOC}\) \((\hbox {eV})\) | \(\mathrm {FWHM}\) \((\hbox {eV})\) | \(\alpha\) | \(A_\mathrm {rel}\) \((\%)\) |
|---|---|---|---|---|---|---|---|
(a) | 0 | Ag | 107.49 | 6.00 | 0.78 | 0.02 | 63.1 |
\(\hbox {Ag}_2\hbox {Ge}\) | 107.34 | 6.00 | 0.67 | 0.02 | 36.4 | ||
P1 | 103.44 | 1.10 | 0.00 | 0.4 | |||
P2 | 97.44 | 1.11 | 0.00 | 0.0 | |||
60 | Ag | 107.48 | 6.00 | 0.78 | 0.02 | 54.6 | |
\(\hbox {Ag}_2\hbox {Ge}\) | 107.33 | 6.00 | 0.67 | 0.02 | 43.9 | ||
P1 | 103.43 | 1.10 | 0.00 | 0.9 | |||
P2 | 97.43 | 1.11 | 0.00 | 0.5 | |||
(b) | 0 | SP | 107.36 | 6.00 | 0.76 | 0.02 | 33.7 |
Ag | 106.88 | 6.00 | 0.78 | 0.02 | 49.8 | ||
\(\hbox {Ag}_2\hbox {Ge}\) | 106.73 | 6.00 | 0.67 | 0.02 | 16.6 | ||
60 | SP | 107.41 | 6.00 | 0.76 | 0.02 | 35.3 | |
Ag | 106.93 | 6.00 | 0.78 | 0.02 | 41.3 | ||
\(\hbox {Ag}_2\hbox {Ge}\) | 106.78 | 6.00 | 0.67 | 0.02 | 23.4 | ||
(c) | 0 | Ag | 107.46 | 6.00 | 0.78 | 0.02 | 92.7 |
\(\hbox {Ag}_2\hbox {Ge}\) | 107.31 | 6.00 | 0.67 | 0.02 | 7.3 | ||
60 | Ag | 107.46 | 6.00 | 0.78 | 0.02 | 78.6 | |
\(\hbox {Ag}_2\hbox {Ge}\) | 107.31 | 6.00 | 0.67 | 0.02 | 21.4 | ||
(d) | 0 | Ag | 107.68 | 6.00 | 0.77 | 0.02 | 100.0 |
60 | Ag | 107.64 | 6.00 | 0.77 | 0.02 | 100.0 |