Figure 7
TEM images of SPSed Mg-15Gd-1Zn bulk under the sintering condition of 450 °C −40 MPa-5 min: (a,b) displaying the lamellar LPSO phase formed during the sintering process; (c) the β1 phase particles, (d,e) showing the selected area electron diffraction (SAED) patterns of LPSO phase and β1 phase, respectively, the beam was parller to12,13,14,15,16 and [0001] (011), the white indices were for the Mg matrix with a hcp structure, and blue indices were for β1 phase with a fcc structure.