Table 1 The related TGA and DTG data of YP, YPM50, YPM60 and MA under nitrogen.

From: A novel form stable phase change material with comb-like cross-linked polyurethane as supporting skeleton

Samples

T5% (°C)a

T50% (°C)b

TPL (°C)c

PL (%/min)d

TPH (°C)e

PH (%/min)f

YP

343.3

410.1

–

–

413.8

− 17.45

MA

185.9

230.8

243.3

− 29.43

–

–

YPM50

190.5

379.0

225.2

− 5.71

411.3

− 10.27

YPM60

189.0

347.0

233.5

− 7.48

410.1

− 7.47

  1. aThe testing temperature when the mass-loss of sample reaches 5 wt%, defined as the initial thermal-degradation temperature.
  2. bThe testing temperature when the mass-loss of sample reaches 50 wt%.
  3. cThe testing temperature of mass-loss peak at low temperature (the range of 0–300 °C).
  4. dThe mass-loss rate of the mass-loss peak at low temperature (the range of 0–300 °C).
  5. eThe testing temperature of mass-loss peak at high temperature (the range of 300–600 °C).
  6. fThe mass-loss rate of the mass-loss peak at high temperature (the range of 300–600 °C).