Table 1 Composition of the multilayer samples used in this work along the saturation magnetization \(M_s\), the uniaxial anisotropy \(H_k\) and the DMI constant value D used in the micromagnetic simulations.

From: Probing of three-dimensional spin textures in multilayers by field dependent X-ray resonant magnetic scattering

Sample

Composition (thickness in nanometers)

\(M_s\) (kA m\(^{-1}\))

\(\mu _0H_k\) (mT)

D (mJ m\(^{-2}\))

S1

\(\vert \vert\)Ta(10)\(\vert\)Pt(8)\(\vert\)[Co(0.8)\(\vert\)Al\(_2\)O\(_3\)(1)\(\vert\)Pt(1)]\(_{\times 20}\vert\)Pt(2)

1373

358

0.9

S2

\(\vert \vert\)Ta(10)\(\vert\)[Al\(_2\)O\(_3\)(1.0)\(\vert\)Co(1)\(\vert\)Pt(1.0)]\(_{\times 20}\vert\)Pt(7)

1278

84

\(-1.7\)

S3

\(\vert \vert\)Pt(10)\(\vert\)[Ir(1.0)\(\vert\)Co(0.8)\(\vert\)Pt(1.0)]\(_{\times 5}\vert\)Pt(3)

1229

640

\(-2.0\)