Table 5 Multi-physics field distribution in the shear plane at different cutting dosages.
From: A new approach to predict microhardness of two-phase in cutting S32760 duplex stainless steel
Experimental group number | \(\varphi /^\circ\) | TAB/K | εAB | \(\dot{\varepsilon }_{AB} /{\text{s}}^{ - 1}\) | KAB/Mpa |
|---|---|---|---|---|---|
1 | 40.56 | 752.35 | 0.4456 | 10,416 | 770.46 |
2 | 40.52 | 772.77 | 0.4458 | 17,509 | 776.68 |
3 | 40.50 | 786.26 | 0.4459 | 24,432 | 781.01 |
4 | 40.47 | 801.58 | 0.4461 | 35,300 | 786.1 |
5 | 40.62 | 753.21 | 0.4452 | 7825.4 | 760.76 |
6 | 40.59 | 774.16 | 0.4454 | 13,156 | 766.26 |
7 | 40.57 | 787.41 | 0.4455 | 18,359 | 770.41 |
8 | 40.54 | 802.46 | 0.4457 | 26,524 | 775.29 |
9 | 40.65 | 754.85 | 0.445 | 6166.1 | 753.02 |
10 | 40.63 | 775.41 | 0.4451 | 10,536 | 758.41 |
11 | 40.60 | 788.62 | 0.4453 | 14,698 | 762.35 |
12 | 40.56 | 803.61 | 0.4456 | 21,229 | 766.99 |
13 | 40.69 | 756.07 | 0.4447 | 5227.4 | 746.97 |
14 | 40.66 | 775.54 | 0.445 | 8787.2 | 752.65 |
15 | 40.63 | 789.57 | 0.4452 | 12,258 | 756 |