Table 1 Classification accuracy of LOPs for disordered and cylindrical structures on \(f=0.33\).
From: Distinguish microphase-separated structures of diblock copolymers using local order parameters
\(r_c\) | LOPs | |||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
\([\sigma _\text{u}]\) | Â | Â | Â | Â | Â | Â | c\([-]\) | Â | Â | Â | Â | Â | Â | Â |
2.850 | \(\overline{A}_1^{1}\) | \(\overline{B}_{2,2,\pi /4}\) | \(\overline{C}\) | \(\overline{D}_{f_2,f_2,f_1}\) | \({F}_{f_2,f_2,1}\) | \(\overline{I}\) | \(\overline{Q}^\text{S}_{4}\) | \(\overline{Q}^\text{L}_{4}\) | \(\overline{LQ}_{4}\) | \(\overline{LQ}^\text{T}_{4}\) | \(\overline{W}^\text{S}_{4}\) | \(\overline{W}^\text{L}_{4}\) | \(\overline{LW}_{4}\) | \(\overline{LW}^\text{T}_{4}\) |
0.975 | 0.964 | 0.814 | 0.915 | 0.728 | 0.967 | 0.974 | 0.972 | 0.699 | 0.684 | 0.573 | 0.560 | 0.580 | 0.554 | |
3.700 | \(\overline{A}_1^{1}\) | \(\overline{B}_{2,2,\pi /4}\) | C | \(\overline{D}_{f_2,f_2,f_1}\) | \(\overline{F}_{f_1,f_1,1}\) | \(\overline{I}\) | \(\overline{Q}^\text{S}_{4}\) | \(\overline{Q}^\text{L}_{6}\) | \(\overline{LQ}_{6}\) | \(\overline{LQ}^\text{T}_{4}\) | \(\overline{W}^\text{S}_{6}\) | \(\overline{W}^\text{L}_{4}\) | \(\overline{LW}_{6}\) | \(\overline{LW}^\text{T}_{4}\) |
0.996 | 0.984 | 0.789 | 0.969 | 0.729 | 0.991 | 0.995 | 0.993 | 0.803 | 0.662 | 0.582 | 0.560 | 0.588 | 0.566 | |
4.700 | \(\overline{A}_2^{1}\) | \(\overline{B}_{2,2,\pi /4}\) | C | \(\overline{D}_{f_2,f_2,f_1}\) | \(\overline{F}_{f_1,f_1,1}\) | \(\overline{I}\) | \(\overline{Q}^\text{S}_{6}\) | \(\overline{Q}^\text{L}_{6}\) | \(\overline{LQ}_{6}\) | \(\overline{LQ}^\text{T}_{6}\) | \(\overline{W}^\text{S}_{8}\) | \(\overline{W}^\text{L}_{4}\) | \(\overline{LW}_{4}\) | \(\overline{LW}^\text{T}_{4}\) |
0.999 | 0.991 | 0.797 | 0.976 | 0.813 | 0.999 | 1.000 | 1.000 | 0.913 | 0.702 | 0.592 | 0.610 | 0.594 | 0.658 | |