Table 2 Experimental measured mechanical properties of materials for fea
Property | Pure | CNT 0.5% | CNT 0.5%, PLA 1% | CNT 0.5%, PLA 1.5% |
|---|---|---|---|---|
Young’s modulus MPa | 2369.5 | 2416.2 | 1383.3 | 921.3 |
Yield strength MPa | 50.3 | 58.9 | 24.4 | 20.6 |
Poisson’s ratio (ν) | 0.193 | 0.186 | 0.1804 | 0.1948 |
Tensile strength MPa | 52.79 | 59.4 | 23.81 | 21.95 |
Flexural strength MPa | 52.07 | 82.92 | 42.95 | 38.29 |
Density g/cm3 | 1.24 | 1.8 | 1.81 | 1.81 |
Fracture energy density MJ/m3 | 6.86 | 8.37 | 10 | 10.57 |