Table 2 Taguchi L₂₇ orthogonal array with experimental values of tensile strength, young’s modulus, and corresponding S/N ratios.

Sl. no.	Composition	Injection temp.	Injection speed	Injection pressure	Tensile strength	Young’s modulus	S/N ratio (tensile strength)	S/N ratio (Young’s modulus)
1	Pure	135	50	30	17.4000	1230.01	24.8605	60.8016
2	Pure	135	50	30	17.6000	1159.14	24.8605	60.8016
3	Pure	135	50	30	17.5000	958.21	24.8605	60.8016
4	Pure	145	60	40	5.7300	820.53	14.9509	58.5081
5	Pure	145	60	40	5.4600	915.14	14.9509	58.5081
6	Pure	145	60	40	5.5950	803.13	14.9509	58.5081
7	Pure	155	70	50	1.2700	753.18	4.5123	58.0529
8	Pure	155	70	50	2.5000	693.88	4.5123	58.0529
9	Pure	155	70	50	1.8850	1080.00	4.5123	58.0529
10	5	135	60	50	58.5000	1006.49	35.1115	60.4710
11	5	135	60	50	55.5000	1018.16	35.1115	60.4710
12	5	135	60	50	57.0000	1162.57	35.1115	60.4710
13	5	145	70	30	39.2000	742.55	31.8098	56.9588
14	5	145	70	30	38.7000	651.66	31.8098	56.9588
15	5	145	70	30	38.9500	730.42	31.8098	56.9588
16	5	155	50	40	24.0000	553.43	26.8233	54.7709
17	5	155	50	40	20.2000	555.02	26.8233	54.7709
18	5	155	50	40	22.1000	535.33	26.8233	54.7709
19	10	135	70	40	54.6966	3561.48	35.2199	69.9311
20	10	135	70	40	60.9992	2652.43	35.2199	69.9311
21	10	135	70	40	57.8479	3453.98	35.2199	69.9311
22	10	145	50	50	38.7000	1637.39	29.7934	64.1668
23	10	145	50	50	25.7000	1433.38	29.7934	64.1668
24	10	145	50	50	32.2000	1858.16	29.7934	64.1668
25	10	155	60	30	17.8000	107.94	23.9027	40.6626
26	10	155	60	30	14.0000	105.84	23.9027	40.6626
27	10	155	60	30	15.9000	110.12	23.9027	40.6626