Table 7 Analysis of the peaks of Figs. 12, 13, and phase identification.

From: A concurrent bioceramic colloid design for dental crowns additive manufacturing by vat photopolymerization

Peak number

Position _°2θ_

d-spacing _Å_

FWHM Total _°2θ_

Miller indices (h k l)

Crystal system

1

24.31

3.66

0.65

011

monoclinic

2

28.28

3.15

0.33

− 111

monoclinic

3

30.28

2.95

0.26

101

tetragonal

4

31.49

2.84

0.40

111

monoclinic

5

34.77

2.58

0.38

002

tetragonal

6

35.25

2.54

0.31

110

tetragonal

7

40.82

2.21

0.19

− 112

monoclinic

8

43.08

2.10

0.31

102

tetragonal

9

50.39

1.81

0.57

− 221

monoclinic

10

55.56

1.65

0.57

− 311

monoclinic

11

59.48

1.55

0.45

103

tetragonal

12

60.11

1.54

0.40

− 203

monoclinic

13

62.81

1.48

0.42

202

tetragonal

14

65.45

1.42

0.66

023

monoclinic

15

73.18

1.29

0.40

004

tetragonal

16

74.38

1.27

0.37

220

tetragonal

17

81.91

1.18

0.88

213

tetragonal

18

83.86

1.15

0.89

114

tetragonal

19

84.90

1.14

0.55

222

tetragonal