Table 9 Mass loss of boronizing specimens, mg.
Specimens codes | Exp. Cond | Mass Loss (mg) | Average mass loss (mg) | COF | Average COF | ||
|---|---|---|---|---|---|---|---|
AISI H13 | a) | 23 | 22.3 ± 2.08 | a) | 0.1 | 0.21 ± 0.115 | |
b) | 24 | b) | 0.33 | ||||
c) | 20 | c) | 0.2 | ||||
A | 850 °C–2 h | a) | 10 | 9.2 ± 1.93 | a) | 0.13 | 0.16 ± 0.030 |
b) | 7 | b) | 0.16 | ||||
c) | 10.6 | c) | 0.19 | ||||
B | 850 °C–4 h | a) | 7 | 7.1 ± 0.85 | a) | 0.12 | 0.15 ± 0.030 |
b) | 8 | b) | 0.18 | ||||
c) | 6.3 | c) | 0.15 | ||||
C | 850 °C–6 h | a) | 6 | 5.7 ± 1.47 | a) | 0.14 | 0.13 ± 0.010 |
b) | 7 | b) | 0.12 | ||||
c) | 4.1 | c) | 0.13 | ||||
D | 950 °C–2 h | a) | 8 | 6.9 ± 1.15 | a) | 0.15 | 0.14 ± 0.012 |
b) | 7 | b) | 0.13 | ||||
c) | 5.7 | c) | 0.15 | ||||
E | 950 °C–4 h | a) | 5 | 4.8 ± 1.31 | a) | 0.12 | 0.11 ± 0.010 |
b) | 6 | b) | 0.1 | ||||
c) | 3.4 | c) | 0.11 | ||||
F | 950 °C–6 h | a) | 2 | 2.9 ± 0.85 | a) | 0.1 | 0.09 ± 0.010 |
b) | 3.7 | b) | 0.08 | ||||
c) | 3 | c) | 0.09 | ||||
G | 1050 °C–2 h | a) | 5 | 5.5 ± 0.50 | a) | 0.12 | 0.12 ± 0.020 |
b) | 6 | b) | 0.1 | ||||
c) | 5.5 | c) | 0.14 | ||||
H | 1050 °C–4 h | a) | 2 | 2.6 ± 0.53 | a) | 0.08 | 0.08 ± 0.010 |
b) | 3 | b) | 0.09 | ||||
c) | 2.8 | c) | 0.07 | ||||
I | 1050 °C–6 h | a) | 1.5 | 1.4 ± 0.10 | a) | 0.06 | 0.06 ± 0.010 |
b) | 1.3 | b) | 0.07 | ||||
c) | 1.4 | c) | 0.05 |