Table 5 Mechanical properties in bending and tension of as prepared and aged samples.

From: Epoxy-based nanocomposites containing sustainable fillers for the realization of speckle patterns for digital image correlation analysis

Sample

Young’s Modulus [GPa]

95% C.I. [GPa]

Poisson’s ratio

95% C.I.

Tensile stress [MPa]

95% C.I. [MPa]

Bending modulus of Elasticity [GPa]

95% C.I. [GPa]

Bending stress [MPa]

95% C.I. [MPa]

Pristine resin

1.92 ± 0.05

0.07

0.36 ± 0.01

0.01

34 ± 11

14

2.66 ± 0.27

0.26

89 ± 7

7

ETiB

2.95 ± 0.19

0.15

0.36 ± 0.01

0.01

21 ± 3

2

3.13 ± 0.37

0.36

42 ± 9

8

Aged ETiB (A)

2.15 ± 0.05

0.05

0.38 ± 0.02

0.03

23 ± 3

4

-

-

-

-

Aged ETiB (B)

2.54 ± 0.43

0.48

0.37 ± 0.01

0.02

21 ± 5

5

-

-

-

-