Table 3 Free energy of adhesion of slurry components with different PVDF latices (\(\Delta G^{IF}_{132}\) is annotated as \(\Delta G^{IF}_{S-H2O-Latex}\) with 1 being the solid sample S, 3 the liquid (\(H_2O\)) and 2 the respective PVDF latex binder).
Solid sample | \(\Delta G^{IF}_{S-H2O-Latex 1}\) | \(\Delta G^{IF}_{S-H2O-Latex 2}\) | \(\Delta G^{IF}_{S-H2O-Latex 3}\) | \(\Delta G^{IF}_{S-H2O-Latex 4}\) |
|---|---|---|---|---|
\((mJ/m^2)\) | ||||
Aluminum CC | -57.8 ± 0.6 | -51.7 ± 0.3 | -44.2 ± 0.4 | -16.8 ± 0.1 |
C65 | -55.9 ± 0.5 | -49.8 ± 0.4 | -42.5 ± 0.6 | -16.4 ± 0.4 |
CMC | -46.1 ± 0.5 | -41.5 ± 0.3 | -35.7 ± 0.1 | -13.5 ± 0.8 |
LNMO | -17.7 ± 0.1 | -15.9 ± 0.1 | -13.7 ± 0.1 | -5.1 ± 0.1 |