Extended Data Fig. 1: Water reactivity using LiTFSI as a supporting salt.
From: Tuning water reduction through controlled nanoconfinement within an organic liquid matrix
Linear sweep voltammograms recorded in acetonitrile in presence of 100 mM LiTFSI with different water contents (1, 2.5, 5, 7.5 and 10% from light to dark blue) using a rotating disc (1,600 rpm) Pt electrode with a 50 mV s−1 sweeping rate. No modification of the onset potential at which water is reduced was observed, independently of the water content, confirming that the trend previously measured for LiClO4 is independent on the nature of the anion.