Table 1 Overview of mechanical properties with average and standard deviation observed in CMD and GA materials as well as typically observed values in plate 7075-T635, Scalmalloy36,37, and AlSi10Mg38 as well as previous efforts to print crack free 707520.

From: Additive manufacturing of a high-performance aluminum alloy from cold mechanically derived non-spherical powder

Material

Modulus (GPa)

Yield strength (MPa)

UTS (MPa)

Elongation (%)

CMD 7075+Zr T6

71.9 ± 1.5

543.3 ± 19.1

597.4 ± 11.1

12.1 ± 2.3

GA 7075+Zr T6

72.4 ± 1.3

527.4 ± 5.5

587.4 ± 6.8

8.4 ± 0.8

Plate Al7075 T635

71.7

372–469

462–538

11.6

AM Al707520

63–66

325–373

383–417

3.8–5.4

Scalmalloy36,37

70–72

475–490

520–580

10–14

AlSi10Mg38

69–70

200–215

300–370

7–10

Back to article page