Fig. 8: Stability and conduction mechanism of Li3InCl6.
From: Design and evaluations of nano-ceramic electrolytes used for solid-state lithium battery
a EIS evaluation under difference cycles, note some curves are superimposed and not visible due to the low root mean square deviation of curves between the plots, and b the calculated porosity is beneficial to Li+ transport through the vacancy, c the CV analyses of the half-cells under different sweep rates, and d the CV analyses of the half-cells under a slow sweep rate of 1 mV s−1.