Figure 3

Thermally assisted electric field control of the UMA in FeGa/PVDF film.

In-plane magnetic hysteresis loops of FeGa/PVDF film measured at 291 K with (a) E = 0 kV cm⁻¹, (b) E = −267 kV cm⁻¹ and (c) E = 267 kV cm⁻¹ applied through the thickness of PVDF. In-plane magnetic hysteresis loops measured at 295 K with (d) E = 0 kV cm⁻¹, (e) E = −267 kV cm⁻¹ and (f) E = 267 kV cm⁻¹. The corresponding angular dependence of normalized remnant magnetization of FeGa/PVDF film measured at (g) 291 K and (h) 295 K with different electric fields applied on PVDF.