Fig. 3
Microstructure and SAED patterns of Ti59.1Zr37Cu2.3Fe1.6 rod with a diameter of 8 mm during in situ heating in the TEM. a As-cast state. b–g In situ heating to temperatures below the α→β transition temperature. The amorphous phase begins to transform to α-Ti at around T = 700 K. h After cooling to room temperature (RT), α-Ti, the equilibrium phase, is only observed. Scale bars in a represent 200 nm for the micrograph and 2 nm−1 for the SAED pattern, respectively. Scale bar in b is 100 nm which also applies to c–h