Fig. 2
From: Spin-induced multiferroicity in the binary perovskite manganite Mn2O3
Magnetic properties of the perovskite-type Mn2O3. a Temperature dependence of DC magnetic susceptibility measured in the field of 500 Oe with both the zero-field-cooling (ZFC) and field-cooling (FC) modes. This curve distinctly demonstrates two magnetic transitions at T1 = 101 K and T2 = 49 K. The inset shows a Curie–Weiss fit of the paramagnetic susceptibility. b, and c shows an effect of applied magnetic field on the above-mentioned magnetic transitions. While the transition at T2 is apparently suppressed by application of a 7 T field, the transition at T1 is very weakly affected by 7 T field. d AC magnetic susceptibility as a function of temperature. The frequency dependent peak around 5 K suggests a short-range ordered magnetic state. e The M–H curve at 2 K showing no saturation of magnetization up to 13 T